Partial Dislocation in Carbon-Vacancy-ordered Nb12Al3C8

Hui Zhang,Xiaohui Wang,Erdong Wu,Yanchun Zhou
DOI: https://doi.org/10.1016/j.scriptamat.2017.10.020
IF: 6.302
2018-01-01
Scripta Materialia
Abstract:Basal dislocations in nanolaminated machinable ternary carbides and nitrides (also known as MAX phases) have been postulated to be the result of shearing M−A bonds, but have not been microscopically confirmed yet. This study on dislocations and stacking faults in C-vacancy-ordered Nb12Al3C8 demonstrates that the basal dislocation core lies between NbC slabs, verifying the shear of Nb−Al bonds. The formation of observed 1/3⟨011¯0⟩ type partial dislocations therefore does not give rise to stacking faults. The frequently observed stacking faults are special intergrowth structures of atomically thin NbC slabs embedded in the Nb12Al3C8 grain.