Understanding the Role of 1/2 ⟨110⟩ Dislocations in Deformation Mechanisms of Single-Crystal High-Entropy Carbide Ceramics from Machine Learning Force Field Simulations

Jie Liu,Kun Luo,Rui Zhou,Qi An
DOI: https://doi.org/10.1021/acsaenm.4c00280
2024-01-01
Abstract:In the realm of ultrahigh-temperature ceramics, high-entropy carbide ceramics face limitations due to their low ductility and limited plasticity. Unraveling their deformation mechanisms is essential for improving the mechanical properties of these ceramics. Here, we focus on the high-entropy ceramics (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C, where we have determined the (110)[110] slip system as the most plausible slip system with the lowest shear strength of 21.79 GPa by developing and employing a machine learning force field. More importantly, we found that ideal shear deformation along this slip system results in the generation of 1/2 < 110 > dislocations, driven by severe lattice distortion and localized chemical disorder. These dislocations subsequently interact, leading to the formation of amorphous regions and vacancies, which ultimately contribute to the failure of this high-entropy ceramic. Our research sheds light on dislocation nucleation, propagation, and interaction in high-entropy ceramics under mechanical deformation. Additionally, it unveils the potential of tailoring the ceramic's composition to improve plasticity by increasing the content of cation ions, which leads to the nucleation of dislocations.
What problem does this paper attempt to address?