Chemical complexity-changed deformation behavior of NiTi-based B2 low- to high-entropy intermetallic compounds: Atomistic simulations

Cheng-Yuan Tsai,Chi-Huan Tung,Chun-Cheng Chen,Shou-Yi Chang

DOI: https://doi.org/10.1016/j.jallcom.2023.171557

IF: 6.2

2023-08-02

Journal of Alloys and Compounds

Abstract:Owing to the high chemical complexity and severe lattice distortion but still long-range ordered structure, the deformation behavior and defect activities of high-entropy intermetallic compounds are worth investigations. Hence in this study, the mechanical properties of NiTi-based low- to high-entropy intermetallic compounds were measured from different orientations at different temperatures simply by using nanoindentations , and compared with the structural evolution and defect activities suggested by molecular dynamics simulations. The deformation of the low-entropy intermetallic compound proceeded with regular martensitic transformation, followed by the heterogeneous nucleation of dislocations at the martensite/austenite interface and the subsequent long-distance gliding accompanied with sharp stress drops. With increasing temperature, a more intense shearing events and marked strength reduction were observed. In comparison, with the introduction of constitutional complexity, the martensitic transition was suppressed. Instead, the early homogeneous nucleation at a relatively small activation volume (acquired from indenting displacement bursts) and small-range activities of abundant defects mediated the smooth stress-strain response and uniform plastic deformation of the high-entropy intermetallic compound. At an elevated temperature, a similar deformation mechanism and the same level of strength were retained in the chemically complex alloy.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering