Abstract:In this study, ternary Al-12Si-0.6Mg material was manufactured by gravity die casting method in induction melting furnace. Microstructure images of alloy were taken on optical microscope after T6 heat treatment. Hardness, yield and tensile strength and breaking elongation of as-cast and heat-treated materials were measured by universal methods. CNC lathe was used for cutting tests and dynamometer was used to measure cutting force. Cutting tests were performed by using different cutting speeds-CS (450-500-550 m/min), feed rates-FR (0.05–0.15-0.25 mm/rev) and constant depth of cut-DOC (1.5 mm). Uncoated (A), CVD-TiCN + TiN (B) and PVD-TiAlN+TiN (C) coated carbide inserts were selected as a cutting tool. In the microstructural observations, it was determined that the structure of the material made up of aluminum rich α, primary and eutectic silicon, δ (Al4FeSi2) and π (Al8Mg3FeSi6) phases. The heat treatment refined the phases in the structure of the alloy. In addition, it has been determined that it improves mechanical properties (hardness, yield and tensile strength) by spheroidizing silicon particles. As a result of the cutting tests, it was detected that the cutting force (CF) reduced with T6 heat treatment at all CS and FR values. The CF, BUE (Built up edge) and BUL (Built up layer) heightened with increasing FR, while it reduced with increasing CS on all cutting tools. CF, BUE and BUL were formed at least in tools A, B and C, respectively. While continuous chip formation was detected in the as-cast part, brittle chip formation was observed in the heat-treated part due to the reduction in breaking elongation of the material.

The Influence of T6 Treatment on Fracture Behavior of Hypereutectic Al-Si HPDC Casting Alloy

Effect of heat treatment on microstructure and tensile properties of 319 aluminum alloy

Effect of chemical composition and T6 heat treatment on microstructure and mechanical properties of a hyper eutectic Al–Si alloy

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Effect of short T6 heat treatment on the microstructure and the mechanical properties of newly developed die-cast Al–Si–Mg–Mn alloys

The Effect of Heat Treatments on the Microstructural Evolution of Twin-Roll-Cast Al-Fe-Si Alloys

The effect of T4 and T6 heat treatments for dynamic impact behavior of casting Mg-Gd-based alloys

Effect of T6I6 treatment on dynamic mechanical behaviour of Al-Si-Mg-Cu cast alloy and impact resistance of its cast motor shell

Effects of T6 heat treatment with residual heat of casting on microstructure and mechanical properties of 319 aluminium alloy castings

The Effect of Solution Treatment on the Si Particles’ Morphology Evolution and the Thermal Conductivity and Tensile Properties of Sb-Modified Al-8Si-0.6Mg Alloys

Processing of T6 heat-treated Al-12Si-0.6Mg alloy

Microstructural Evolution and Strengthening Behavior of High-Pressure Die-Cast High-Cu Al-Si-Cu-Mg Alloy with T5 Treatment

Evolution of precipitation and mechanical properties of high-pressure vacuum die- cast AlSi10MgMn alloy in T5 and T6 heat treated states

Microstructure, Tensile Properties and Fractography of A356 Alloy under As-Cast and T6 Obtained with Expendable Pattern Shell Casting Process

Characterization of high-pressure die-cast hypereutectic Al-Si alloys based on microstructural distribution and fracture morphology

Influence of Y Content and T6 Heat Treatment on the Organization and Mechanical Properties of Cast A356 Aluminum Alloy

Microstructure and mechanical property of high power laser powder bed fusion AlSi10Mg alloy before and after T6 heat treatment

Tensile properties and fractography of A356 alloy produced by EPSC-VL process

Effect of T6 heat treatment on microstructure and mechanical properties of large-weight aluminum alloy flywheel housing parts formed by local-loading squeeze casting

Effect of T6 heat treatment on microstructure and mechanical properties of Al–18Si–10Cu–10Ni–5Mn–5Mg alloy prepared by laser-directed energy deposition

Effects of magnesium and copper additions on tensile properties of Al-Si-Cr die casting alloy under as-cast and T5 conditions