Abstract:Polymerization induced self-assembly (PISA) is a promising route to prepare nanoparticles with various morphologies at high solid content and has attracted intensive attention in the past few decades. In this study, an amphiphilic maleamic acid-alpha-methyl styrene copolymer (MAA-alt-AMS, macro-initisurf) was synthesized, which acted as a macroinitiator and emulsifier for the emulsion polymerization induced self-assembly of acrylate monomers to prepare core-shell nanoparticles comprised of MAA-alt-AMS as the shell and poly(methyl methacrylate-ran-butyl acrylate) as the core. Using DPPH as a radical scavenger, the thermal-induced decomposition of MAA-alt-AMS chains was investigated. The results showed that the polymer chains of MAA-alt-AMS can be clefted to generate macromolecular radicals to initiate the polymerization of monomers at a temperature above 70 degrees C. The chain scission of MAA-alt-AMS can be regarded as the first-order reaction and the activation energy of decomposition is determined to be 62.81 kJ mol(-1). The emulsion PISA of acrylate monomers initiated by the macro-initisurf shows a high conversion, which can reach almost 100% with a mass ratio of the macro-initisurf to monomers of 2 : 5 and the obtained spherical nanoparticles possess a shell-core structure and narrow size distribution (PDI < 0.05). The size of nanoparticles can be tuned from 80 to 200 nm by changing the macro-initisurf content, monomer ratio and reaction temperature, while the thickness of the shell remained around 20-30 nm regardless of reaction conditions. The MAA-alt-AMS triggered emulsion PISA has the advantages of a short reaction time (can be finished within 2 h) and a high solid content (up to 50%), and has great potential in large scale industrial application.

Polymerization-induced Self-Assembly of Acrylonitrile Via ICAR ATRP

One‐step Synthesis of Hyperbranched Polyethylene Macroinitiator and Its Block Copolymers with Methyl Methacrylate or Styrene Via ATRP

Study on Kinetics of Controlled/living Radical Polymerization of Acrylonitrile by RAFT Technique

In Situ Crosslinking of Nanoparticles in Polymerization-Induced Self-Assembly Via ARGET ATRP of Glycidyl Methacrylate.

Icar Atrp Of Acrylonitrile Under Ambient And High Pressure

ICAR ATRP Polymerization-Induced Self-Assembly Using a Mixture of Macroinitiator/Stabilizer with Different Molecular Weights.

Development of ICAR ATRP-Based Polymerization-Induced Self-Assembly and Its Application in the Preparation of Organic-Inorganic Nanoparticles

Polymerization-Induced Self-Assembly (Pisa) Using Icar Atrp At Low Catalyst Concentration

Controlled/Living Radical Polymerization of Acrylonitrile: an Overview

Synthesis of PAN with adjustable molecular weight and low polydispersity index (PDI) value via reverse atom transfer radical polymerization

Ab Initio RAFT Emulsion Copolymerization of Styrene and Acrylonitrile

Preparation of polyacrylonitrile with improved isotacticity and low polydispersity

Polymerization-Induced Self-Assembly of Conjugated Block Copoly(phenylacetylene)s

Graft Polymerization of 2-Hydroxyethyl Methacrylate Via ATRP with Poly(acrylonitrile-Co-p-chloromethyl Styrene) As a Macroinitiator

Preparation of Block Copolymer Self‐Assemblies via Pisa in a Non‐Polar Medium Based on Rcmp

One-Step Photocontrolled Polymerization-Induced Self-Assembly (Photo-PISA) by Using In Situ Bromine-Iodine Transformation Reversible-Deactivation Radical Polymerization

Polymerization Techniques in Polymerization-Induced Self-Assembly (PISA)

Group-Transfer Polymerization-Induced Self-Assembly (GTPISA) in Non-polar Media: An Organocatalyzed Route to Block Copolymer Nanoparticles at Room Temperature

Preparation of core-shell nanoparticles <i>via</i> emulsion polymerization induced self-assembly using a maleamic acid--methyl styrene copolymer as a macro-initisurf

Exploring the Topological Effect of Linear and Cyclic Macroctas During Polymerization-Induced Self-Assembly (PISA)

Aqueous Photoiniferter Polymerization of Acrylonitrile