Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Fabrication and Abrasive Wear Behavior of ZrO2-SiC-Al2O3 Ceramic

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Tribological properties and wear resistance mechanism of WC-ZrO2-Al2O3 ceramics

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Abrasive wear behavior of Sialon ceramic

Mechanical properties and wear behaviors of Cu-doped zirconia-toughened alumina ceramics

Fabrication and Characterization of ZrO_2/SiC Composite Materials

Evidence into practice: the mental health hurdle is high

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Erosive Wear Performance and Mechanism of Engineering Ceramic Materials

Preparation, mechanical properties, and toughening mechanisms of SiCw/SiCp‐reinforced zirconia‐toughened alumina ceramics

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Microstructure and Wear Behaviour of Ceramic Particles Strengthening Nial Based Composite

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-SiCp ceramics

Mechanical and Tribological Behaviors of Hot-Pressed SiC/SiCw-Y2O3 Ceramics with Different Y2O3 Contents

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Microstructure, mechanical and friction-wear properties of SiC-WC composite with Al and C as sintering aids

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

In-situ friction and wear study of SiCα/SiCβ and Al2O3-TiC-Co composite ceramics

Tribological Behavior of Liquid Phase Sintered SiC Ceramics Under Dry Condition

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO2–Al2O3-SiCp ceramics