Syngas Production Via Coal Char-Co 2 Fluidized Bed Gasification and the Effect on the Performance of LSCFN//LSGM//LSCFN Solid Oxide Fuel Cell

Hai-Bin Li,Na Xu,Yi-Hua Fang,Hui Fan,Ze Lei,Min-Fang Han

DOI: https://doi.org/10.1016/j.jmst.2017.06.001

2018-01-01

Abstract:Fluidized bed reactor is widely used in coal char-CO 2 gasification. In this work, the production of syngas by using a fluidized bed gasification technique was first investigated and then the effect of the produced syngas on the performance of the solid oxide fuel cell with a configuration of La 0.4 Sr 0.6 Co 0.2 Fe 0.7 Nb 0.1 O 3-δ //La 0.8 Sr 0.2 Ga 0.83 Mg 0.17 O 3-δ //La 0.4 Sr 0.6 Co 0.2 Fe 0.7 Nb 0.1 O 3-δ （LSCFN//LSGM//LSCFN）was studied. During the syngas production, we found that the volume fraction of CO increased with the increment of gasification temperature, and it reached a maximum value of 88.8%, corresponding to a composition of 0.76% H 2 , 88.8% CO, and 10.44% CO 2 , when the ratio of oxygen mass flow rate to that of coal char（MO2/Mchar） increased to 0.29. In the following utilization of the produced syngas in solid oxide fuel cells, it was found that the increasing CO volume fraction in the syngas results in a gradual increase of the peak power density of the LSCFN//LSGM//LSCFN cell. The maximum peak power density of 410 m W/cm~2 was achieved for the syngas produced at 0.29 of M O2 /M char . In the stability test, the cell voltage decreased by 4% at a constant current density of 0.475 A/cm~2 after 54 h when fueled with the syngas with the composition of 0.76% H2, 88.8% CO, and 10.44% CO 2 .It reveals that a carbon deposition with the content of 13.66% in the anode is attributed to the cell performance degradation.