Cr3+ and Nb5+ Co-Doped Ti2Nb10O29 Materials for High-Performance Lithium-Ion Storage

Chao Yang,Shu Yu,Yu Ma,Chunfu Lin,Zhihao Xu,Hua Zhao,Shunqing Wu,Peng Zheng,Zi-Zhong Zhu,Jianbao Li,Ning Wang

DOI: https://doi.org/10.1016/j.jpowsour.2017.06.026

IF: 9.2

2017-01-01

Journal of Power Sources

Abstract:Ti2Nb10O29 is an advanced anode material for lithium-ion batteries due to its large specific capacity and high safety. However, its poor electronic/ionic conductivity significantly limits its rate capability. To tackle this issue, a Cr3+-Nb(5+)co-doping is employed, and a series of Cr(x)Ti(2-2x)Nb(10+x)O29 compounds are prepared. The co-doping does not change the Wadsley-Roth shear structure but increases the unit-cell volume and decreases the particle size. Due to the increased unit-cell volumes, the co-doped samples show increased Li+-ion diffusion coefficients. Experimental data and first-principle calculations reveal significantly increased electronic conductivities arising from the formation of impurity bands after the co-doping. The improvements of the electronic/ionic conductivities and the smaller particle sizes in the co-doped samples significantly contribute to improving their electrochemical properties. During the first cycle at 0.1 C, the optimized Cr0.6Ti0.8Nb10.6O29 sample delivers a large reversible capacity of 322 mAh g(-1) with a large first-cycle Coulombic efficiency of 94.7%. At 10 C, it retains a large capacity of 206 mAh while that of Ti2Nb10O29 is only 80 mAh Furthermore, Cr0.6Ti0.8Nb10.6O29 shows high cyclic stability as demonstrated in over 500 cycles at 10 C with tiny capacity loss of only 0.01% per cycle. (C) 2017 Elsevier B.V. All rights reserved.