Abstract:Stress relaxation cracking (SRC) is considered one of the major failure mechanisms for 347H stainless steel welds at elevated service temperatures or during post weld heat treatment (PWHT), especially within the heat-affected zone (HAZ). This work focuses on the characterization of SRC susceptibility within 347H physically simulated arc welded HAZ at elevated temperatures. A four-step SRC thermomechanical test in combination with finite element modeling (FEM) of the welding and testing processes is developed to establish a susceptibility map for HAZ. The test first runs a thermal cycle with three different peak temperatures (1335, 1275, and 1150 °C) to duplicate representative HAZ subzone microstructures, followed by time-to-failure examination under a variety of pre-stress (260–600 MPa) and pre-strain conditions (0.03–0.19) as a function of reheat temperatures between 750 and 1050 °C. With the aid of FEM, SRC susceptibility maps are generated to identify the threshold stress, plastic strain, and creep strain as a function of test temperature. It was found out that HAZ subzone with a lower peak temperature (1150 °C) appears to be slightly less susceptible to SRC than the other two subzones that experienced higher peak temperatures. Generally, time-to-fracture reduces with increasing initially applied stress and strain for all test temperatures. The pre-stress thresholds decrease from about 500 to 330 MPa as the testing temperature increases from 800 to 1050 °C, while the corresponding initial plastic strain thresholds reduces from 0.15 to 0.06. The SRC susceptibility was also evaluated through the Larson–Miller Parameter (LMP) analysis as a function of plastic strain, initial stress and starting stress upon reaching the testing temperature, respectively. The 1050 °C test with a high pre-applied strain (0.1) exhibits an extremely short time to failure (t = 3 s) that lies outside the general trend in LMP analysis. Additionally, it was identified that a plastic strain above 0.07 is identified to significantly reduce the bulk creep strain tolerance to fracture and therefore increases SRC susceptibility. Hardness measurement and fractography analysis indicated that the strain aging of niobium carbonitrides and other potential phases in conjunction with intergranular precipitates contributes to an increase in microhardness and increased intergranular cracking susceptibility.

Local Approach to Stress Relaxation Cracking in a AISI 316L-Type Austenitic Stainless Steel: Tomography Damage Quantification and FE Simulations

Intergranular Damage During Stress Relaxation in Aisi 316L-Type Austenitic Stainless Steels: Effect of Carbon, Nitrogen and Phosphorus Contents

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Damage and Cracking Prediction of AISI 410 Martensitic Stainless Steel at Elevated Temperatures

In-situ observation of strain evolution and ratchetting of growing fatigue cracks

Stress Relaxation Cracking in 347H Stainless Steel Arc Welds: Susceptibility Evaluation of Heat-Affected Zone

A micromechanical analysis of intergranular stress corrosion cracking of an irradiated austenitic stainless steel

ICONE23-1741 POLYCRYSTALLINE SIMULATIONS OF LOCAL STRESS DISTRIBUTIONS IN NEUTRON IRRADIATED AUSTENITIC STAINLESS STEELS

Thermo-mechanical FE model with memory effect for 304L austenitic stainless steel presenting microstructure gradient

Nanoindentation Investigation of Chloride-Induced Stress Corrosion Crack Propagation in an Austenitic Stainless Steel Weld

Micro-mechanics investigation of heterogeneous deformation fields and crack initiation driven by the local stored energy density in austenitic stainless steel welded joints

Intergranular precipitation behavior and its influence on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal during long-term aging

LOW CYCLE FATIGUE FRACTURE FOR 316ti STAINLESS STEEL IN HIGH TEMPERATURE AND PRESSURE WATER

Towards Understanding Stress Corrosion Cracking of Austenitic Stainless Steels Exposed to Realistic Sea Salt Brines

Crack Propagation and Strain-Induced Α’-Martensite Transformation in Selective Laser Melting 316L Stainless Steels

Intergranular stress distributions in polycrystalline aggregates of irradiated stainless steel

Stress Corrosion Cracking Behavior of Cold-Drawn 316 Austenitic Stainless Steels in Simulated Pwr Environment

Visualization and Location Determination of Pit Initiation Sites in Martensitic Stainless Steel during Corrosion-Fatigue Cyclic Plastic Deformation

Anisotropic Ductile Fracture Of A Stainless Steel Under Biaxial Loading: Experiments And Predictions

Finite Element Simulation and Experimental Verification of Internal Stress of Quenched AISI 4140 Cylinders

Quantifications of crack constraint effects in an austenitic steel