Na 3 V 2 (PO 4 ) 3 /C nanofiber bifunction as anode and cathode materials for sodium-ion batteries

Qing Zhu,Bo Nan,Yang Shi,Yinggang Zhu,Sisi Wu,Liqing He,Yonghong Deng,Liping Wang,Quanqi Chen,Zhouguang Lu

DOI: https://doi.org/10.1007/s10008-017-3627-y

IF: 2.747

2017-01-01

Journal of Solid State Electrochemistry

Abstract:Na 3 V 2 (PO 4 ) 3 /C composite nanofibers are prepared successfully through a coaxial electrospinning technique and subsequent calcination. The diameter of the prepared nanofibers is uniformly distributed (about 100∼200 nm), and the composite nanofibers (NF-NVP/C) contain Na 3 V 2 (PO 4 ) 3 nanofibers and carbon nanofibers, and Na 3 V 2 (PO 4 ) 3 nanoparticles with diameters of 5–10 nm are embedded into the composite nanofibers. The NF-NVP/C anode exhibits a high reversible capacity 189.9 mAh/g at a current rate of 0.2 C (1 C=118 mA/g) in the voltage range of 0.01–3.00 V (vs. Na + /Na). Even at high rates of 5 and 10 C, this anode displays discharge capacities of 105.1 and 80.4 mAh/g at the second cycle and capacity retentions of 83 and 77% after 200 and 500 cycles, respectively. A sodium-ion full cell with NF-NVP/C as the electroactive material of both positive and negative electrodes presents two average operating voltages at ∼0.5 and ∼1.5 V and delivers a reversible capacity of 106.2 mAh/g at a current density of 100 mA/g in a voltage range of 0.01–4.00 V. The outstanding electrochemical performance is attributed to the unique nanofiber structure and uniform distribution of NVP nanoparticles in the highly conductive carbon matrix.