Abstract:The applications of silica aerogels are restricted due to their intrinsic fragile property. Polymerization of di-isocyanates can be templated onto the mesoporous surface of the –NH2 group modified silica clusters, resulting in the conformal crosslinked coating on surface of silica clusters. Aminopropyltriethoxysilane (APTES), as the silica co-precursor and amine group modification agent, is involved containing tetramethyl orthosilicate (TMOS) silica precursor, while hexamethylene diisocyanate (HDI) is incorporated as the polymer crosslinking agent. The effects of different amounts of APTES on the physicochemical properties of the resulting crosslinked aerogels are investigated. The results show that the optimized APTES/TMOS volume ratio can be determined at 0.5:1. The resulting optimal crosslinked silica aerogel possesses large BET specific surface area of 150.9 m2/g, low thermal conductivity of 0.037 W/(m·K), and the Young's modulus is as large as 18 MPa under strain of 4.2%, much higher than that in the previously published works. The polymerization reaction mechanism forming the polyurethane chains has also been proposed. In addition, the interactions between silica clusters and polymer chains are studied by molecular mechanics and molecular dynamics. The interactions are mainly dependent on non-bonding energy, and the electrostatic energy has decisive impact on the combination of silica clusters and polymer chains. The density field of C, H, N, O, and Si elements overlaps with each other, indicating that the polymer crosslinked silica aerogel maintains typical three-dimensional porous structure. The N element enriches in the region between silica clusters, further verifying the formation –CONH–(CH2)6–CONH- polyurethane chains, which is actually responsible for the much enhanced mechanical property.

In-situ synthesis and textural evolution of the novel carbonaceous SiC/mullite aerogel via polymer-derived ceramics route

In Situ Formation of the TiCN Phase in SiBCN Ceramic Aerogels Enabling Superior Thermal and Structural Stability Up to 1800 °C.

Fabrication of SiCN(O) Aerogel Composites with Low Thermal Conductivity by Wrapping Mesoporous Aerogel Structures over Mullite Fibers

Evolution of the Novel C/SiO2/SiC Ternary Aerogel with High Specific Surface Area and Improved Oxidation Resistance

Novel Al2O3–SiO2 composite aerogels with high specific surface area at elevated temperatures with different alumina/silica molar ratios prepared by a non-alkoxide sol–gel method

Preparation of the Novel B4C–SiC Composite Aerogel with High Compressive Strength and Low Thermal Conductivity

Facile synthesis of mullite fiber/alumina composite aerogel with enhanced bending strength and controllable thermal insulation performance

Enhancing the thermal insulation properties of polymer-derived SiCN(O) ceramic aerogels with a polysilazane-precursor design

Synthesis and Textural Evolution of Mesoporous Si3N4 Aerogel with High Specific Surface Area and Excellent Thermal Insulation Property Via the Urea Assisted Sol-Gel Technique

Ultralight, thermal insulating, and high-temperature-resistant mullite-based nanofibrous aerogels

Synthesis of Al2O3-SiO2 aerogels with low thermal conductivity and high strength by methyltriethoxysilane as a silica precursor

Fabrication of the SiC/HfC Composite Aerogel with Ultra-Low Thermal Conductivity and Excellent Compressive Strength

Isocyanate-crosslinked silica aerogel monolith with low thermal conductivity and much enhanced mechanical properties: Fabrication and analysis of forming mechanisms

Synthesis and characterization of SiO2-Al2O3 composite aerogel using inorganic aluminum salt as raw material

Flexible SiC nanowire/mullite fiber composite aerogel with adjustable strength based on micromechanical design

Investigation on textural and structural evolution of the novel crack-free equimolar Al2O3-SiO2-TiO2 ternary aerogel during thermal treatment

Preparation and Structural Evolution of SiOC Preceramic Aerogel During High-Temperature Treatment

Preparation and Characterization of C/Al 2 O 3 Composite Aerogel with High Compressive Strength and Low Thermal Conductivity

Synthesis of a novel Al 2 O 3 –SiO 2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum

Design and preparation of novel Y2O3-SiO2 composite aerogels for high-temperature thermal insulators

Rational design of a novel mullite aerogel with extremely high mechanical strength and anti-oxidation behavior for advanced thermal protection in extreme environments