Single-crystalline TiO 2 nanoparticles for stable and efficient perovskite modules
Yong Ding,Bin Ding,Hiroyuki Kanda,Onovbaramwen Jennifer Usiobo,Thibaut Gallet,Zhenhai Yang,Yan Liu,Hao Huang,Jiang Sheng,Cheng Liu,Yi Yang,Valentin Ianis Emmanuel Queloz,Xianfu Zhang,Jean-Nicolas Audinot,Alex Redinger,Wei Dang,Edoardo Mosconic,Wen Luo,Filippo De Angelis,Mingkui Wang,Patrick Dörflinger,Melina Armer,Valentin Schmid,Rui Wang,Keith G. Brooks,Jihuai Wu,Vladimir Dyakonov,Guanjun Yang,Songyuan Dai,Paul J. Dyson,Mohammad Khaja Nazeeruddin
DOI: https://doi.org/10.1038/s41565-022-01108-1
IF: 38.3
2022-01-01
Nature Nanotechnology
Abstract:Despite the remarkable progress in power conversion efficiency of perovskite solar cells, going from individual small-size devices into large-area modules while preserving their commercial competitiveness compared with other thin-film solar cells remains a challenge. Major obstacles include reduction of both the resistive losses and intrinsic defects in the electron transport layers and the reliable fabrication of high-quality large-area perovskite films. Here we report a facile solvothermal method to synthesize single-crystalline TiO 2 rhombohedral nanoparticles with exposed (001) facets. Owing to their low lattice mismatch and high affinity with the perovskite absorber, their high electron mobility and their lower density of defects, single-crystalline TiO 2 nanoparticle-based small-size devices achieve an efficiency of 24.05% and a fill factor of 84.7%. The devices maintain about 90% of their initial performance after continuous operation for 1,400 h. We have fabricated large-area modules and obtained a certified efficiency of 22.72% with an active area of nearly 24 cm 2 , which represents the highest-efficiency modules with the lowest loss in efficiency when scaling up.