Abstract:C/C-ZrC-SiC composites were produced by the joint processes of chemical liquid-vapor deposition (CLVD) and precursor infiltration and pyrolysis (PIP), and the effects of deposition period in CLVD process on the preparation, microstructure and anti-ablation property were studied. The results displayed the non-woven layers of the composites was preferred to be densified in CLVD method, but the subsequent PIP process could fill the pores of the fiber webs. Thus the joint technologies reduced the porosity of the composites and improved the content of ceramics. Meanwhile, the insufficient deposition in CLVD process led to large amounts of defects, which were not densified fully in the following PIP. However, the excessive deposition of CLVD filled the pores remarkably, so the channels for precursor infiltration in the subsequent PIP were reduced. When the deposition period was 8 h, the sample C8P9 had a low porosity, high ceramics content and uniform distribution, which was responsible for its outstanding ablation resistance. After ablation for 60 s, sample C8P9 was damaged slightly, and its mass and linear ablation rate was 1.22 x 10(-3) g/s and 1.07 x 10(-3) mm/s. The ablation surface was divided into four regions, and the different oxide coatings were generated on these regions. These coatings could provide effective protection for the composites, which made a significant contribution to improve the ablation resistance.

Effects of SiC Interphase on the Mechanical and Ablation Properties of C/C-ZrC-ZrB 2 -Sic Composites Prepared by Precursor Infiltration and Pyrolysis

Microstructure, Interfacial and Mechanical Properties of SiC Interphase Modified C/C-SiC Composites Prepared by Reactive Melt Infiltration

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Effects of Polymer-Derived ZiC Interlayer on Mechanical Properties and Ablation Performance of C/C-ZiC-ZrC-SiC Composites Prepared by RMI

Preparation and Ablation Properties of SiC Nanowire-Reinforced ZrC–SiC Coating-Matrix Integrated C/C Composites

The Effect of PyC/SiC Compound Interphase on the Properties of PIP SiC/SiC Composite

Preparation and properties of C/C-ZrC-SiC-ZrB2 composites via polymer infiltration and pyrolysis

Mechanical Properties and Ablation Behavior of C/C-ZrC and C/C-ZrC-SiC Composites Prepared by Precursor Infiltration and Pyrolysis Combined with Chemical Vapor Infiltration

Ablative and Mechanical Properties of C/C‐SiC‐ZrC Composites Modified with PyC/SiC and PyC/BN Interface Layers

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Microstructure and Ablation Behavior of SiC Coated C/C–SiC–ZrC Composites Prepared by a Hybrid Infiltration Process

Improved Ablation Resistance of C/Sic-Zrb2 Composites Via Polymer Precursor Impregnation and Pyrolysis

Mechanical properties and oxidation resistance of SiC f/CVI-SiC composites with PIP-SiC interphase

Mechanical, Oxidation and Ablation Properties of C/(C-SiC)CVI-(ZrC-SiC)PIP Composites

Microstructure and Ablation Property of C/C-ZrC-SiC Composites Fabricated by Chemical Liquid-Vapor Deposition Combined with Precursor Infiltration and Pyrolysis

Effects of the Single Layer Cvd Sic Interphases on the Mechanical Properties of the Sicf/Sic Composites Fabricated by Pip Process

Effect of ZrC–SiC Content on Microstructure and Ablation Properties of C/C Composites

Preparation and Ablation Properties of SiC Modified C/C Composites

Ablation of advanced C/C-ZrC-SiC leading edge composites

Effects of Zro2 Interphase on Mechanical and Microwave Absorbing Properties of Sicf/Sic Composites

Ablation Properties of C/C-Zrc-Sic Composites by the Precursor Infiltration Pyrolysis