Abstract:Huge amount of flue gas desulphurization (FGD) gypsum not only occupies the farmland but also causes severe pollution to the surrounding environment. The most effective way to achieve a high-value utilization of FGD gypsum is to prepare short columnar α-calcium sulfate hemihydrate (α-HH) since short columnar crystals show better mechanical strength than needle-like ones. Here, malic acid, a prolific, inexpensive and environment-friendly modifier was explored for the first time to effectively tune the crystal morphology of α-HH prepared from FGD gypsum in glycerol-water-NaCl solutions. When the concentration of malic acid reached 18.54 × 10-4 mol/kg, α-HH crystals with an average aspect (length-to-diameter) ratio of 1.9 (compared to 29.4 in the absence of malic acid) were prepared. The selective complexation of malic acid with Ca active sites on different α-HH crystal planes played a dominant role in the α-HH crystal morphology transformation, which was then explained by the surface broken bonds theory for the first time. The broken bond number per active Ca atom (Nbper Ca) and broken bond density of Ca atoms (DbCa) on the (2 0 4) end plane were larger than those on the (0 2 0) or (2 0 0) side planes. Therefore, the (2 0 4) end plane was more reactive with organics, resulting in the preferential adsorption of malic acid on the end planes, which reduced the specific surface energy of (2 0 4) and led to an increased exposure of this plane and a decreased exposure of (0 2 0) or (2 0 0) side planes in the final α-HH crystals. Consequently, using malic acid as modifier, the α-HH crystal gradually transformed from a needle-like shape to a short columnar one. This work provided important insights into and perspectives for the selection of crystal modifiers and explanation of the mechanism during the preparation of calcium-containing crystals with controllable morphology.

Synthesis of alpha hemihydrate particles with lithium and carboxylates via the hydrothermal method

Effect Of Potassium Sodium Tartrate And Sodium Citrate On The Preparation Of Alpha-Calcium Sulfate Hemihydrate From Flue Gas Desulfurization Gypsum In A Concentrated Electrolyte Solution

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Synthesis of α-calcium sulfate hemihydrate submicron-rods in water/n-hexanol/CTAB reverse microemulsion

Preparation of α-calcium sulfate hemihydrate from FGD gypsum in K, Mg-containing concentrated CaCl2 solution under mild conditions

Direct transformation of calcium sulfite to α-calcium sulfate hemihydrate in a concentrated Ca–Mg–Mn chloride solution under atmospheric pressure

A Facile Method to Control the Structure and Morphology of Α-Calcium Sulfate Hemihydrate

Characterization and Precipitation Mechanism of Α-Calcium Sulfate Hemihydrate Growing out of FGD Gypsum in Salt Solution

Experimental Study and Mechanism Analysis of Preparation of α-Calcium Sulfate Hemihydrate from FGD Gypsum with Dynamic Method

Controllable synthesis of snowflake‐like α‐calcium sulfate hemihydrate microstructures using Na2EDTA as morphology modifier

Rapid synthesis of alpha calcium sulfate hemihydrate whiskers in glycerol-water solution by using flue-gas-desulfurization gypsum solid waste

Influence of Seed Crystal and Modifier on the Morphology of α-calcium Sulfate Hemihydrate Prepared by Salt Solution Method in Pilot Scale

Influences of Citric Acid on the Metastability of Α-Calcium Sulfate Hemihydrate in CaCl2 Solution

Effect of Butane Diacid on Crystal Morphology and Reaction Process of α-Calcium Sulfate Hemihydrate in Preparation from Flue Gas Desulphurization Gypsum

Preparation of α-High Strength Gypsum from Flue Gas Desulfurization Gypsum Pretreated by Hydrothermal-aging Method

Direct transformation of FGD gypsum to calcium sulfate hemihydrate whiskers: Preparation, simulations, and process analysis

Coordinated disposal of FGD gypsum and power plant concentrated brine via preparation of α-hemihydrate gypsum

Effect of particle size on the transformation kinetics of flue gas desulfurization gypsum to α-calcium sulfate hemihydrate under hydrothermal conditions

Effect of mixed cation acetate electrolyte on synthesis of α‐hemihydrate gypsum from phosphogypsum

Preparation of α-CaSO4·½H2O with tunable morphology from flue gas desulphurization gypsum using malic acid as modifier: A theoretical and experimental study