Effect of Glass Additions on Ca 0.8 Sr 0.2 TiO 3 Ceramics as Dielectrics for a Cylindrical Dielectric Barrier Discharge Reactor in CO 2 Plasma

Song Xiaozhen,Zhang Yong,Qu Fuyang,Wang Xiangrong
DOI: https://doi.org/10.1016/S1875-5372(17)30050-4
2016-01-01
Rare Metal Materials and Engineering
Abstract:The Ca0.8Sr0.2TiO3 ceramics with different amounts of glass addition were prepared by liquid phase sintering and used as dielectric barriers in a cylindrical dielectric barrier discharge reactor to decompose carbon dioxide at atmospheric pressure. Results show that the surface resistivity increases with increasing glass content. While the dielectric constant does not change obviously with the increase of the glass content in the investigated temperature range. The scanning electron microscope observations indicate that both the grain size and the thickness of intergranular glassy phases increase with the increase of the glass content. More importantly, the conversion rate and conversion efficiency of carbon dioxide improve with the increase of glass content in the ceramics. Furthermore, a combined discharge analysis and dielectric characterization are modeled with a Malter effect approach. From this model, it is possible to interpret the relationship between the conversion characteristics and the glass content in the ceramic samples.
What problem does this paper attempt to address?