Spatial Grain Growth And Composition Evolution During Sulfurizing Metastable Wurtzite Cu2znsns4 Nanocrystal-Based Coatings

Xu Liu,Jialiang Huang,Fangzhou Zhou,Fangyang Liu,John A. Stride,Xiaojing Hao

DOI: https://doi.org/10.1021/acs.chemmater.6b04603

IF: 10.508

2017-01-01

Chemistry of Materials

Abstract:A drawback of nanocrystal-based processing, that leads to the notoriously poor crystallinity of pure-sulfide Cu2ZnSnS4 absorber, was recently reported to be effectively overcome by the annealing of thin films made from the ink of metastable wurtzite Cu2ZnSnS4 nanocrystals in a combined S and SnS atmosphere. However, the formation pathway from nanometer-sized crystals in the wurtzite phase to micrometersized grains with the kesterite phase during this process still lacks in-depth study. In this work, the spatial grain growth and composition evolution during the sulfurization of wurtzite nanocrystal coatings are systematically investigated by classifying samples into temperature and time series. In the process of heating up, the reversible migration of Cu and Zn species contributes to a continuous growth of kesterite Cu2ZnSnS4 grains on the surface. At higher temperature, a fast phase-transition growth from wurtzite Cu2ZnSnS4 nanoparticles to kesterite grains is also directly observed in the region away from the surface. After reaching 580 degrees C, the thin film experiences impressive decomposition and reorganization changes as a function of time, which cause the formation of an absorber with good crystallinity and homogeneous compositional distribution. The solar cell device, fabricated by employing this pure-sulfide Cu2ZnSnS4 absorber from wurtzite nanocrystal-based coatings, demonstrated an energy conversion efficiency of 6.0% in the absence of an antireflection coating.