Abstract:Plasma fusion devices will require plasma-facing components (PFCs) which can withstand the extreme environment at the edge of a hot fusion plasma. Despite the excellent properties of tungsten(W) as a hard refractory metal, adverse effects such as embrittlement, melting, and morphological evolution have been observed in W when it is bombarded by a high-fluence of low-energy ions including helium. This study investigates the effect of helium ion bombardment on pure tungsten and a tungsten heavy alloy (W-HA)(NAECOMET 1000). Pure tungsten and NAECOMET 1000 samples were implanted with 3 keV helium ions with fluences ranging from 1.15×1021m−2 to 2.21×1022m−2 , using Plasma Immersion Ion Implantation (PIII). After PIII treatment, samples were analysed using scanning electron microscopy (SEM) and atomic force microscopy (AFM), which revealed differences in surface morphology and topography. Although the melting and cracking of the Ni/Cu binder phase in the NAECOMET 1000 samples was seen under all implantation conditions, the Ni/Cu presence did somewhat slow the formation of W fuzz in comparison to pure tungsten. X-ray diffraction (XRD) studies showed peak shifts increasing with helium ion fluence for both the pure W and NAECOMET 1000 samples, as well as increase in mean crystallite size, confirming the distortion of the lattice. XPS compositional analysis showed a strong oxidation (>97 % ) near the metal surface, after helium PIII treatment, for both pure W and NAECOMET 1000 W-HA samples. Some conclusions about the potential suitability of W-HA materials for fusion plasma PFCs are drawn.

Effects of Low Energy Helium Plasma Irradiation on Potassium Doped Tungsten

Properties of Potassium Doped and Tantalum Containing Tungsten after Heavy Ion Irradiation

Effect of Potassium Doping on the Thermal Shock Behavior of Tungsten

Effect of Helium Plasma Irradiation on Microstructures and Mechanical Properties of Tungsten

Helium effects on the surface and subsurface evolutions in single-crystalline tungsten

Effects of Deuterium Plasma Exposure and Helium Ions Irradiation on Nanoindentation Hardness of Tungsten

Effects of Low Energy and High Flux Helium/Hydrogen Plasma Irradiation on Tungsten As Plasma Facing Material

Fuzz Nanostructure and Erosion on Tungsten–vanadium Alloys Exposed to Helium Plasma in the STEP Linear Plasma Device

Effect of helium pre-implantation on the thermal shock performance of tungsten

Helium Irradiation Behavior of Tungsten-Niobium Alloys under Different Ion Energies

Irradiation hardening behaviors of large-scale hot rolling potassium-doped tungsten alloy under synergistic irradiations of Fe11+ ion combined with deuterium and helium plasmas

Effect of Surface Quality on Hydrogen/helium Irradiation Behavior in Tungsten

Decreased surface blistering and deuterium retention in potassium potassium-doped tungsten exposed to deuterium plasma following ion irradiation

The Influence of Coherent Oxide Interfaces on the Behaviors of Helium (He) Ion Irradiated ODS W

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Microstructure and Helium Irradiation Performance of W–ZrC/Sc 2 O 3 Composites Prepared Spark Plasma Sintering

Helium-induced Hardening Effect in Polycrystalline Tungsten

Radiation Effects in Tungsten and Tungsten-Copper Alloys Treated with Compression Plasma Flows and Irradiated with He Ions

Helium Radiation Blistering Mechanisms in Tungsten: Ion Channeling Effects

Helium plasma immersion ion implantation studies of tungsten and tungsten heavy alloys for fusion plasma facing components

Microstructure Evolution and Effect on Deuterium Retention in Oxide Dispersion Strengthened Tungsten During He+ Irradiation