Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

Experimental And Numerical Investigations Of The Interlaminar Shear Properties Of Carbon/Carbon Composites

Experimental and Numerical Investigations of Bend Properties of Carbon/Carbon Composites

A new simulation method for characterizing the shear behavior of needled carbon fiber composites

Experimental and numerical studies on low-velocity impact of laminated C/SiC structures

Damage and Failure of Laminated Carbon-Fiber-Reinforced Composite under Low-Velocity Impact

Investigation on the off-axis tensile failure behaviors of 3D woven composites through a coupled numerical-experimental approach

Experimental and Simulation Study on Failure of Thermoplastic Carbon Fiber Composite Laminates under Low-Velocity Impact

Experimental Investigation on Interlaminar and In-Plane Shear Damage Evolution of 2D C/SiC Composites Using Acoustic Emission and X-ray Computed Microtomography

Study on Interlaminar Shear and Damage Behavior of Carbon Fiber Composites with Short Fiber Interleaves: 2. Micro-Mechanical Simulation

An Experimental and Numerical Investigation on Low-Velocity Impact Damage and Compression-after-impact Behavior of Composite Laminates

Effect of Shear Strain Rate on Interlaminar Shear Behavior of 2D-C/sic Composites: A Damage Transition from Notch Ends Initiation to Gauge Section Initiation

Compressive Failure Analysis of Unidirectional Carbon/epoxy Composite Based on Micro-Mechanical Models

Micromechanical Modeling of Longitudinal Tensile Behavior and Failure Mechanism of Unidirectional Carbon Fiber/aluminum Composites Involving Fiber Strength Dispersion

Experimental and Multiscale Numerical Investigation on Failure Behavior of Satin Woven Carbon/carbon Composites Subjected to Pin-Loading

Micromechanical Modeling of Damage Evolution and Mechanical Behaviors of CF/Al Composites under Transverse and Longitudinal Tensile Loadings.

Experiment and mesoscopic modelling on the dynamic compressive behaviors of a new carbon fiber-reinforced cement-based composite

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

Damage Model for Predicting Shear Strength of Carbon/carbon Composite Fastener Based on Post-Failure Behavior

Experimental Study on Carbon Fiber/epoxy Laminates under Dynamic Tensile and Their Damage Analysis

Multiscale Numerical Scheme on Shear Failure Feature of 3dowc/cs Bar Incorporating Microlevel Uncertainties and Coupled Constitutive Behavior

Experimental and numerical simulation study on Near-edge/On-edge Low-Velocity impact and residual compressive strength of T300/69 laminates