Abstract:Nitrogen-doped activated carbons (N-ACs) with controlled nitrogen doping and analogous microporous structures were prepared by pyrolysis of poly((pyrrole-2,5-diyl)-co-(benzylidene)1 (PPCB). The obtained N-ACs were thoroughly characterized using HRTEM, FESEM, BET, FTIR and)PS for their morphology, surface area and chemical composition. The N-ACs were further used to fabricate supercapacitors, and their comprehensive electrochemical properties, such as cyclic voltammograms, galvanostatic charge-discharge, electrochemical impedance spectrum, electrochemical capacitive performance, power density and long cyclic stability, were studied. The galvanostatic charge-discharge (GC) measurements on N-ACs produced at 700 degrees C and 800 degrees C show a high specific capacitance (up to 525.5 F g(-1) and an energy density of ca. 262.7 W h kg(-1) at 0.26 A g(-1)) in alkaline media (2 M KOH). More importantly, the capacitance remains practically identical when the scan rate was increased from 0.26 to 26.31 A g(-1). The observed capacitance retention (similar to 99.5%) of N-ACs is remarkably stable for electrodes even after 4000 cycles, due to the presence of nitrogen at the surface and in the graphitic edge planes. The nitrogen content plays a significant role in producing micropore dominated ACs and in facilitating the transfer of ions through pores on the surface. The precursor (PPCB) used is cheap and can easily be prepared, making it promising for the large-scale production of N-ACs as excellent electrode materials for supercapacitors.

Resin-Derived Activated Carbons with In-Situ Nitrogen Doping and High Specific Surface Area for High-Performance Supercapacitors

Nitrogen-doped porous carbons with nanofiber-like structure derived from poly (aniline-co-p-phenylenediamine) for supercapacitors

High Specific Capacitance Electrode Material for Supercapacitors Based on Resin-Derived Nitrogen-Doped Porous Carbons

Synthesis of Nitrogen-Doped Polymeric Resin-Derived Porous Carbon for High Performance Supercapacitors

A Facile Preparation Of Nitrogen/Phosphorus Co-Doped Carbon Materials From Urea Formaldehyde Microspheres For High-Performance Supercapacitors

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Nitrogen-doped porous carbon with a hierarchical structure prepared for a high performance symmetric supercapacitor

Nitrogen-doped Porous Carbon with a 3D Network Structure Produced from Resorcinol-Gelatin-formaldehyde Co-Polymers and Its Use As an Electrode Material for Supercapacitors

Nitrogen-doped hierarchical porous carbon materials derived from diethylenetriaminepentaacetic acid (DTPA) for supercapacitors

Nitrogen-doped porous carbon materials derived from ionic liquids as electrode for supercapacitor

Porous N Self-Doped Carbon Materials for High-Performance Supercapacitors Via Nanosized Silica Template Combined with Pyrolysis Method

Promising Biomass-Derived Nitrogen-Doped Porous Carbon for High Performance Supercapacitor

Schiff-Base/Resin Copolymer under Hypersaline Condition to High-Level N-Doped Porous Carbon Nanosheets for Supercapacitors

Promising Nitrogen-Rich Porous Carbons Derived from One-Step Calcium Chloride Activation of Biomass-Based Waste for High Performance Supercapacitors

Sustainable supercapacitors of nitrogen-doping porous carbon based on cellulose nanocrystals and urea

Nitrogen-Doped Activated Carbons Derived From A Co-Polymer For High Supercapacitor Performance

Biomass Derived Nitrogen Doped Carbon with Porous Architecture As Efficient Electrode Materials for Supercapacitors

N-doped layered porous carbon electrodes with high mass loadings for high-performance supercapacitors

Shape-Controlled Synthesis Of Porous Carbons For Flexible Asymmetric Supercapacitors

N-Doped Porous Carbon Derived from Solvent-Free Synthesis of Cross-Linked Triazine Polymers for Simultaneously Achieving CO2 Capture and Supercapacitors.

Facile 3D Nitrogen‐Doped Hierarchical Porous Carbon for High‐Performance Supercapacitors