Abstract:N-doped porous carbon (N-PC) is considered as a promising candidate for electrochemical energy storage. However, the complicated multistep process is the biggest bottleneck. Here, a facile one-step strategy was employed to fabricate the N-doped porous carbon via the co-pyrolysis of urea and poly(acrylic acid- co -maleic acid) sodium salt (PAMS) without the protection of inert gas at 550 °C. When the mass ratio of urea to PAMS is 4:1, the microstructure and electrochemical properties of the as-prepared sample (N-4PC) are obviously improved compared with that of the direct carbonization of PAMS (PC). N-4PC presents salient peculiarities with much more mesopores, higher specific surface area of 181.5 m 2 g −1 far more than PC (23.6 m 2 g −1 ), and its nitrogen content is up to 10.61 at. %. In a three-electrode configuration using 6 M KOH, owing to the synergistic effect of pyridinic N, pyrrolic N and graphitic N atoms, N-4PC shows an outstanding specific capacity of 210 F g −1 far more than that of PC (93 F g −1 ) at 1 A g −1 , and a significant capacity retention rate of 79 % much higher than PC (47 %) at 20 A g −1 . Furthermore, the symmetric supercapacitor fabricated by N-4PC delivers an attractive specific capacitance of 140 F g −1 at 1 A g −1 , and 4.9 Wh kg −1 energy density when the power density is 265 W kg −1 in 6 M KOH. The equipment achieves superior cycle stability with capacity retention of 97 % after 7000 cycles at 1 A g −1 . Additionally, N-4PC also achieves great energy densities of 6.7 Wh kg −1 at the power density of 372.3 W kg −1 in 1 M H 2 SO 4 and 12.5 Wh kg −1 at the power density of 521.5 W kg −1 in 1 M Li 2 SO 4 . The fabricated nitrogen-doped porous carbon material has a great potential application prospect in energy storage equipment.

Sustainable supercapacitors of nitrogen-doping porous carbon based on cellulose nanocrystals and urea

Nitrogen-doped porous carbon materials derived from ionic liquids as electrode for supercapacitor

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Full-faradaic-active nitrogen species doping enables high-energy-density carbon-based supercapacitor

Nitrogen-doped porous carbon derived from ginkgo leaves with remarkable supercapacitance performance

Nitrogen-doped coal-based microporous carbon material co-activated by HCOOK and urea for high performance supercapacitors

N, P codoped carbon nanosheets derived from rice husk for supercapacitors with high energy density

Nitrogen-doped carbons derived from cotton pulp for improved supercapacitors

Facile 3D Nitrogen‐Doped Hierarchical Porous Carbon for High‐Performance Supercapacitors

Balancing the gravimetric and volumetric capacitance of nitrogen-enriched lignin porous carbon for high performance supercapacitors

Nitrogen source-mediated cocoon silk-derived N, O-doped porous carbons for high performance symmetric supercapacitor

Fishbone-derived N-doped hierarchical porous carbon as an electrode material for supercapacitor

Synthesis of Nitrogen-Doped Polymeric Resin-Derived Porous Carbon for High Performance Supercapacitors

Chitin derived nitrogen-doped porous carbons with ultrahigh specific surface area and tailored hierarchical porosity for high performance supercapacitors

N-doped layered porous carbon electrodes with high mass loadings for high-performance supercapacitors

Synthesis of Nitrogen-Doped Porous Carbon Nanofibers As an Efficient Electrode Material for Supercapacitors.

Facile synthesis of porous carbon materials with extra high nitrogen content for supercapacitor electrodes

Nitrogen-doped cornstalk-based biomass porous carbon with uniform hierarchical pores for high-performance symmetric supercapacitors

Supercapacitors based on a nitrogen doped hierarchical porous carbon fabricated by self-activation of biomass: excellent rate capability and cycle stability

Molten Salt-Confined Construction of Nitrogen-Doped Hierarchical Porous Carbon for High-Performance Supercapacitors

One-step synthesis of polymer based N-doped porous carbon with enriched nitrogen content and its enhanced electrochemical properties in supercapacitors