Abstract:Nitrogen-doped activated carbons (N-ACs) with controlled nitrogen doping and analogous microporous structures were prepared by pyrolysis of poly((pyrrole-2,5-diyl)-co-(benzylidene)1 (PPCB). The obtained N-ACs were thoroughly characterized using HRTEM, FESEM, BET, FTIR and)PS for their morphology, surface area and chemical composition. The N-ACs were further used to fabricate supercapacitors, and their comprehensive electrochemical properties, such as cyclic voltammograms, galvanostatic charge-discharge, electrochemical impedance spectrum, electrochemical capacitive performance, power density and long cyclic stability, were studied. The galvanostatic charge-discharge (GC) measurements on N-ACs produced at 700 degrees C and 800 degrees C show a high specific capacitance (up to 525.5 F g(-1) and an energy density of ca. 262.7 W h kg(-1) at 0.26 A g(-1)) in alkaline media (2 M KOH). More importantly, the capacitance remains practically identical when the scan rate was increased from 0.26 to 26.31 A g(-1). The observed capacitance retention (similar to 99.5%) of N-ACs is remarkably stable for electrodes even after 4000 cycles, due to the presence of nitrogen at the surface and in the graphitic edge planes. The nitrogen content plays a significant role in producing micropore dominated ACs and in facilitating the transfer of ions through pores on the surface. The precursor (PPCB) used is cheap and can easily be prepared, making it promising for the large-scale production of N-ACs as excellent electrode materials for supercapacitors.

A Facile Preparation Of Nitrogen/Phosphorus Co-Doped Carbon Materials From Urea Formaldehyde Microspheres For High-Performance Supercapacitors

Nitrogen-doped porous carbons with nanofiber-like structure derived from poly (aniline-co-p-phenylenediamine) for supercapacitors

Resin-Derived Activated Carbons with In-Situ Nitrogen Doping and High Specific Surface Area for High-Performance Supercapacitors

High Specific Capacitance Electrode Material for Supercapacitors Based on Resin-Derived Nitrogen-Doped Porous Carbons

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Nitrogen-containing ultramicroporous carbon nanospheres for high performance supercapacitor electrodes

Synthesis of Nitrogen-Doped Polymeric Resin-Derived Porous Carbon for High Performance Supercapacitors

Facile synthesis of N/P co-doped carbons with tailored hierarchically porous structures for supercapacitor applications

Nitrogen-doped porous carbon with a hierarchical structure prepared for a high performance symmetric supercapacitor

Nitrogen, Phosphorus Co-doped Carbon Obtained from Amino Acid Based Resin Xerogel as Efficient Electrode for Supercapacitor

Nitrogen-doped porous carbon materials derived from ionic liquids as electrode for supercapacitor

Nitrogen-doped hierarchical porous carbon materials derived from diethylenetriaminepentaacetic acid (DTPA) for supercapacitors

Sustainable Synthesis of Phosphorus- and Nitrogen-Co-doped Porous Carbons with Tunable Surface Properties for Supercapacitors

Biomass Derived Nitrogen Doped Carbon with Porous Architecture As Efficient Electrode Materials for Supercapacitors

N-doped layered porous carbon electrodes with high mass loadings for high-performance supercapacitors

Porous N Self-Doped Carbon Materials for High-Performance Supercapacitors Via Nanosized Silica Template Combined with Pyrolysis Method

Facile 3D Nitrogen‐Doped Hierarchical Porous Carbon for High‐Performance Supercapacitors

Nitrogen-Doped Activated Carbons Derived From A Co-Polymer For High Supercapacitor Performance

Sustainable supercapacitors of nitrogen-doping porous carbon based on cellulose nanocrystals and urea

Nitrogen-doped Porous Carbon with a 3D Network Structure Produced from Resorcinol-Gelatin-formaldehyde Co-Polymers and Its Use As an Electrode Material for Supercapacitors

Promising Nitrogen-Rich Porous Carbons Derived from One-Step Calcium Chloride Activation of Biomass-Based Waste for High Performance Supercapacitors