Abstract:Nitrogen-doped hierarchical porous carbons (NHPCs) with controllable nitrogen content were prepared via a template-free method by direct carbonization of melamine-resorcinol-terephthaldehyde networks. The synthetic approach is facile and gentle, resulting in a hierarchical pore structure with modest micropores and well-developed meso-/macropores, and allowing the easy adjusting of the nitrogen content in the carbon framework. The micropore structure was generated within the highly cross-linked networks of polymer chains, while the mesopore and macropore structure were formed from the interconnected 3D gel network. The as-prepared NHPC has a large specific surface area of 1150 m(2).g(-1), and a high nitrogen content of 14.5 wt.%. CO2 adsorption performances were measured between 0 degrees C and 75 degrees C, and a high adsorption capacity of 3.96 mmol.g(-1) was achieved at 1 bar and 0 degrees C. Moreover, these nitrogen-doped hierarchical porous carbons exhibit a great potential to act as electrode materials for supercapacitors, which could deliver high specific capacitance of 214.0 F.g(-1) with an excellent rate capability of 74.7% from 0.1 to 10 A.g(-1). The appropriate nitrogen doping and well-developed hierarchical porosity could accelerate the ion diffusion and the frequency response for excellent capacitive performance. This kind of new nitrogen-doped hierarchical porous carbons with controllable hierarchical porosity and chemical composition may have a good potential in the future applications. (C) 2016 Elsevier Inc. All rights reserved.

N-Doped Porous Carbon Derived from Solvent-Free Synthesis of Cross-Linked Triazine Polymers for Simultaneously Achieving CO2 Capture and Supercapacitors.

Facile Synthesis of Nitrogen-Doped Porous Carbons for CO 2 Capture and Supercapacitors

Nitrogen-doped porous carbons with nanofiber-like structure derived from poly (aniline-co-p-phenylenediamine) for supercapacitors

Adenine-Derived Nitrogen-doped Porous Carbon for High-Performance Supercapacitor Electrodes and Carbon Dioxide Capture

Nitrogen-doped Porous Carbon for Excellent CO2 Capture: A Novel Method for Preparation and Performance Evaluation

Synthesis of Nitrogen-Doped Polymeric Resin-Derived Porous Carbon for High Performance Supercapacitors

Porous N Self-Doped Carbon Materials for High-Performance Supercapacitors Via Nanosized Silica Template Combined with Pyrolysis Method

Nitrogen-doped hierarchical porous carbon materials derived from diethylenetriaminepentaacetic acid (DTPA) for supercapacitors

Nitrogen-doped Porous Carbon with a 3D Network Structure Produced from Resorcinol-Gelatin-formaldehyde Co-Polymers and Its Use As an Electrode Material for Supercapacitors

Resin-Derived Activated Carbons with In-Situ Nitrogen Doping and High Specific Surface Area for High-Performance Supercapacitors

N,S-containing polycondensate-derived porous carbon materials for superior CO<sub>2</sub> adsorption and supercapacitor

Nitrogen-doped porous carbon with a hierarchical structure prepared for a high performance symmetric supercapacitor

Shape-Controlled Synthesis Of Porous Carbons For Flexible Asymmetric Supercapacitors

Template-free Synthesis of Nitrogen-Doped Hierarchical Porous Carbons for CO2 Adsorption and Supercapacitor Electrodes.

Promising Biomass-Derived Nitrogen-Doped Porous Carbon for High Performance Supercapacitor

Nitrogen-doped Porous Carbon Materials Generated Via Conjugated Microporous Polymer Precursors for CO2 Capture and Energy Storage

A Simple CaCO 3 -Assisted Template Carbonization Method for Producing Nitrogen Doped Porous Carbons As Electrode Materials for Supercapacitors

N-doped porous carbon with directional oriented channel structure derived from biomass peach gum/poly( o -phenylenediamine) composite for high-performance supercapacitors

High Specific Capacitance Electrode Material for Supercapacitors Based on Resin-Derived Nitrogen-Doped Porous Carbons

Ultrahigh Surface Area N-Doped Hierarchically Porous Carbon for Enhanced CO2 Capture and Electrochemical Energy Storage

Biomass Derived Nitrogen Doped Carbon with Porous Architecture As Efficient Electrode Materials for Supercapacitors