Abstract:In this study, we investigated the impact of aluminium ion (Al 3+ ) incorporation on the microstructure and the phase transformation of the magnesium silicate hydrate system. The magnesium silicate hydrate system with aluminium was prepared by mixing magnesium oxide and silica fume with different aluminium ion contents (the Al/Si molar ratios of 0.01, 0.02, 0.05, 0.1, 0.2) at room temperature. The high degree of polymerization of the magnesium silicate hydrate phases resulted in the limited incorporation of aluminium in the structure of magnesium silicate hydrate. The silicon-oxygen tetrahedra sites of magnesium silicate hydrate layers, however, were unable to substitute for silicon sites through inverted silicon-oxygen linkages. The increase in aluminium ion content raised the degree of polymerization of the magnesium silicate hydrate phases from 0.84 to 0.92. A solid solution was formed from residual aluminum-amorphous phases such as hydroxyl-aluminum and magnesium silicate hydrate phases. X-ray diffraction (XRD), field emission scanning electron microscope (F-SEM), and 29 Si and 27 Al MAS NMR data showed that the addition of Al 3+ promotes the hydration process of MgO and has an obvious effect on the appearance of M-S-H gel. The gel with low aluminum content is fluffy, while the gel with high aluminum content has irregular flakes. The amount of Al 3+ that enters the M-S-H gel increased with the increase of Al 3+ content, but there was a threshold: the highest Al/Si molar ratio of M-S-H gel can be maintained at about 0.006.

Microstructure and characterization of hydrothermal synthesis of Al-substituted tobermorite

Incorporation of Al and Na in Hydrothermally Synthesized Tobermorite

Synthesis of Al-Substituted 11Å Tobermorite from Aegirine-Augite Syenite Potash Ores by Hydrothermal Reaction at 300°C

Hydrothermal synthesis and characterization of core/shell ALOOH microspheres

Effect of Aluminum Incorporation on the Reaction Process and Reaction Products of Hydrated Magnesium Silicate

Influences of cross-linking and Al incorporation on the intrinsic mechanical properties of tobermorite

Morphology Evolution in Hydrothermal Synthesis of Mesoporous Alumina

Effect of Al Addition on Properties of Al 2 O 3 -Sic-c Dry Ramming Mixes for BF Trough

Effects of aluminum on micro-sized pore structure of porous MoAlB ceramics fabricated via reactive synthesis

Effect of Solubility of Aluminum Sources and Iron Loadings on the Structure and Morphology of FeAIPO-5 Molecular Sieves

Synthesis, Characterization and Hexavalent Chromium Adsorption Characteristics of Aluminum- and Sucrose-Incorporated Tobermorite.

Microstructure and compression properties of fine Al2O3 particles dispersion strengthened molybdenum alloy

Effect of Aluminum on the Formation of Zeolite MCM-22 and Kenyaite

Effect of Aluminum on Hollow Ceramic Microspheres Synthesized Using SHS Quenched Technology

Synthesis Of A Hierarchical Micro/Mesoporous Structure By Steam-Assisted Post-Crystallization

Effect of Calcination Temperature on the Thermal and Hydrothermal Stability of Al-Pillared Montmorillonite

Microstructure and High Temperature Deformation Behavior of the Mo-ZrO 2 Alloys

Fluoride Ions Assistant Synthesis of Extremely Hydrothermal Stable Al-Sba-15 with Controllable Al Content

Synthesis of Aluminum Titanate Solid Solution by Solid State Reaction of Fine Commercial Al2o3, Tio2 and Mgo Powders

Preparation of MCM-48 Materials with Enhanced Hydrothermal Stability

Size and Morphology Controlled Synthesis of Boehmite Nanoplates and Crystal Growth Mechanisms