Abstract:It’s a critical issue for the successful commercialization of solid oxide fuel cells (SOFCs) to achieve long-term thermal stability without significant performance degradation. Current work reports a cost-competitive and scalable method for modifying porous Gadolinia doped ceria (GDC) barrier layers, to obtain an almost-dense, sintering-active, and Sr-blocking cathode/electrolyte interface, by growing nanoparticles in-situ on porous surfaces. The cell performance only deteriorates by ~0.5% after 20 times thermal cycles as the temperature fluctuated between 200 and 750 ℃, which is more prominent enhancement than ~16% for pristine cell, and exhibits higher initial performance. The hydrothermal modified symmetric cell shows ~60% polarization resistance decrease and well-attached cathode/electrolyte interfaces after ~1200 hours of operation, exhibiting excellent stability while the pristine cell interfaces peeled off. The performance improvements and prolonged operation mechanisms are discussed and mainly attributed to the almost-dense barrier layer and robust cathode/electrolyte interfaces.It’s a critical issue for the successful commercialization of solid oxide fuel cells (SOFCs) to achieve long-term thermal stability without significant performance degradation. Current work reports a cost-competitive and scalable method for modifying porous Gadolinia doped ceria (GDC) barrier layers, to obtain an almost-dense, sintering-active, and Sr-blocking cathode/electrolyte interface, by growing nanoparticles in-situ on porous surfaces. The cell performance only deteriorates by ~0.5% after 20 times thermal cycles as the temperature fluctuated between 200 and 750 ℃, which is more prominent enhancement than ~16% for pristine cell, and exhibits higher initial performance. The hydrothermal modified symmetric cell shows ~60% polarization resistance decrease and well-attached cathode/electrolyte interfaces after ~1200 hours of operation, exhibiting excellent stability while the pristine cell interfaces peeled off. The performance improvements and prolonged operation mechanisms are discussed and mainly attributed to the almost-dense barrier layer and robust cathode/electrolyte interfaces.

Pore Orientation of the Gadolinia‐doped Ceria Cathode Interlayer for a Tubular SOFC Using Dip‐coating

In Situ Densification of Gadolinium-Doped Ceria Interlayer by Infiltration Process in SOFC

Low Temperature Deposited (ce,gd)o2−x Interlayer for La0.6Sr0.4Co0.2Fe0.8O3 Cathode Based Solid Oxide Fuel Cell

Highly dense and ultrathin gadolinia-doped ceria interlayer for enhanced performance of large-area anode-supported solid oxide fuel cell

Preparation, Evaluation, and Application of SUS430/441 Interconnect with Mn-Co Coating in Solid Oxide Fuel Cells

Solid oxide fuel cell with a spin-coated yttria stabilized zirconia/gadolinia doped ceria bi-layer electrolyte

Performance and Stability Analysis of SOFC Containing Thin and Dense Gadolinium-Doped Ceria Interlayer Sintered at Low Temperature

Enhancing the performance of doped ceria interlayer for tubular solid oxide fuel cells

Hierarchically oriented macroporous anode-supported solid oxide fuel cell with thin ceria electrolyte film.

Tubular SOFC with Hollow Fiber Ceramic Support and Inner Coating

Densification of Ce0.9Gd0.1O2-δ Interlayer to Improve the Stability of La0.6Sr0.4Co0.2Fe0.8 O3-δ/Ce0.9Gd0.1O2-δ Interface and SOFC

Conducting Property and Performance Evaluation of LNF As Cathode Current Contact Layer in Solid Oxide Fuel Cell

Enhancement of the Cathode/electrolyte Interface by a Sintering-Active Barrier Layer for Solid Oxide Fuel Cells

Lower Down Both Ohmic and Cathode Polarization Resistances of Solid Oxide Fuel Cell Via Hydrothermal Modified Gadolinia Doped Ceria Barrier Layer

Electrical and microstructural characterization of ceramic gadolinium-doped ceria electrolytes for ITSOFCs by sol-gel route

Synthesis and Characterization of (gd, Y)-Doped Ceria Electrolytes for Solid Oxide Fuel Cell

Preparation and Characterization of Y2O3–Sm2O3 Co-Doped Ceria Electrolyte for IT-SOFCs

Enhanced Cathode/Electrolyte Interface by a Nano-Modified Barrier Layer for Solid Oxide Fuel Cells

Microstructures, conductivities, and electrochemical properties of Ce0.9Gd0.1O2 and GDC–Ni anodes for low-temperature SOFCs

Bifunctional Ce0.9Gd0.09M0.01O2−δ (M = Fe, Cu) interlayers with micro-doping for high-performance solid oxide fuel cells

Palladium and ceria infiltrated La0.8Sr0.2Co0.5Fe0.5O3-δ cathodes of solid oxide fuel cells