Abstract:In order to improve the ablation and oxidation resistance of C/C–ZrC–SiC composites in wide temperature domain, "Z-pins like" Zr–Si–B–C multiphase ceramic rods are prepared in the matrix. The influence of different sintering temperatures on the microstructure of ceramic rods and the ablative behavior of heterogeneous composites are studied. The results showed that the ZrB2 and SiC phases are formed in the sintered matrix, and the increase of sintering temperature is beneficial to improve the density of the ceramic rods. The ablation properties of samples have been greatly improved. The mass and linear ablation rate are 0.8 mg/s and 3.85 μm/s, respectively, at an ablation temperature of 3000 °C and an ablation time of 60 s. After ablation, the matrix surface is covered with SiO2 and ZrO2 mixed oxide films. This is due to the preferential oxidation of "Z-pins like" Zr–Si–B–C multiphase ceramic rods in the ablation process, and B2O3 melt, SiO2 melt, borosilicate glass, ZrSiO4 melt and ZrO2 oxide film can be generated successively from the low-temperature segment to the ultra-high temperature segment. These oxidation products can be used as compensation oxide melts for the healing of cracks and holes on the matrix surface in different temperature ranges and effectively prevent the external heat from spreading into the matrix. Therefore, C/C–ZrC–SiC composites with "Z-pins like" Zr–Si–B–C multiphase ceramic rods achieve ablation resistance in wide temperature domain.

Comparison of Microstructure and Ablation Behavior of Si-Mo-Ti/Al/Zr Infiltrated C/C Composites Prepared at Different Infiltration Temperature

Microstructure and Ablation Behavior of Zr-based Ultra-High-temperature Gradient Composites

Ultra-high-temperature ablation behavior of SiC–ZrC–TiC modified carbon/carbon composites fabricated via reactive melt infiltration

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Influence of Reactive Melt Infiltration Parameters on Microstructure and Properties of Low Temperature Derived Cf/ZrC Composites

Microstructure and ablation behaviour of C/C-SiC-ZrC-Cu composites prepared by reactive melt infiltration

Microstructure and mechanical properties of Zr3Al3C5-based ceramics synthesized by Al-Si melt infiltration

Ablation behavior and mechanisms of 3D Cf/ZrB2-SiC composite applied in long-term temperature up to 2400 °C

Ablation behavior and mechanisms of 3D C<sub>f</sub>/ZrB<sub>2</sub>-SiC composite applied in long-term temperature up to 2400 C

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Microstructure, Mechanical and Ablation Properties of Transpiration Cooling Applied to C/C-SiC Composite for Novel Anti-ablation Material

Effect of heat treatment on the microstructure and ablation performance of C/C–SiC composites containing ZrSi 2 –Si

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

The Microstructure and Mechanical Property of Mo(Si, Al)2-SiC Composite Prepared by Infiltrating Melt Aluminum

Structural characteristics and ablative behavior of C/C–ZrC–SiC composites reinforced with “Z-pins like” Zr–Si–B–C multiphase ceramic rods

Microstructure and Mechanical Properties of Mo-ZrC-Cu Composites Synthesized by Reactive Melt Infiltration of Zr-Cu Melt into Porous Mo2C Preforms at 1300 °C

Ablation behavior of ZrC-SiC-ZrB2 and ZrC-SiC inhibited carbon/carbon composites components under ultrahigh temperature conditions

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

Effect of Infiltrated Eutectic AlSi on the Microstructure and Properties of C/C Composites

Microstructure and properties of C/C–ZrC composites with matrix modification by slurry infiltration

Effect of infiltration time on the microstructure and mechanical properties of C/C-SiC composite prepared by Si‐Zr10 alloyed melt infiltration