Abstract:Gas tungsten arc welding (GTAW) is a widely used process in marine and offshore applications to produce high-quality dissimilar welded joints (DWJs). However, the structural integrity of the welded joint depends on the heat input and filler metal application. This study investigated the microstructure–mechanical integrity and residual stresses of a multipass GTAW joint between super duplex stainless steel (sDSS 2507) and Inconel 625 (IN-625) utilizing ERNiCrMo-3 filler and two heat inputs (0.73 and 1.4 kJ/mm). This is a typical dissimilar joint found in oil and gas pipelines, and risers used to extract hydrocarbons. To understand the effect of the microstructure evolution on the mechanical behavior, the microstructure of the lower heat input (LHI) and higher heat input (HHI) weldments was compared. The optical image and secondary electron spectroscopy revealed an austenitic microstructure with an equiaxed, columnar, and cellular morphology in the LHI and HHI weld zones, with a Ni weight percentage of 52.40 pct. An unmixed zone (UZ) was found at the LHI and HHI weld zones and sDSS 2507 base metal interface but not at the IN-625 interface. NbC and Laves phases were found in the interdendritic region by energy-dispersive X-ray spectroscopy. Mechanical testing, including microhardness behavior, tensile properties, and impact toughness, was conducted in various weld regions following standard procedures at room temperature. The study also used deep hole drilling (DHD) methods to assess residual stresses of both LHI and HHI weld zone and determine whether heat input influenced these stresses. The LHI and HHI specimens' average ultimate tensile strength and percent elongation values were determined to be 800 ± 7 MPa and 27 ± 2 pct and 857 ± 5 MPa and 29 ± 3 pct, respectively. The microhardness maps demonstrated variations in the weld zones for both heat input weldments. The weld zone's hardness varied from 260 to 360 Hv 0.5 , with an average of 280 ± 6 Hv 0.5 for LHI and 300 ± 4 Hv 0.5 for HHI weldment. Impact toughness for the LHI weldment was 155 ± 3 and 160 ± 2 J for the cap and root regions, respectively, while it was 185 ± 7 and 195 ± 3 J for the HHI weldment. The DHD approach was utilized to analyze the distribution of residual stresses in the weld zone of both heat input weldments. Both the LHI and HHI joints showed a significant variation in residual stresses, with the HHI weldment exhibiting higher residual stress magnitudes for both tangential (21 pct) and longitudinal (23 pct) directions. The sDSS 2507/IN-625 DWJ was optimally fabricated without significant defects and with adequate mechanical performance to be considered for use in oil and gas pipelines and risers used in hydrocarbon extraction in accordance with ASTM specifications.

Microstructure of a Safe-End Dissimilar Metal Weld Joint (SA508-52-316L) Prepared by Narrow-Gap GTAW

Microstructure, Hardness, and Residual Stress of the Dissimilar Metal Weldments of SA508-309L/308L-304L

Investigation on microstructural and mechanical integrity of GTAW dissimilar welded joint of IN 718/ASS 304L using Ni-based filler IN 625 using EBSD and DHD techniques

Microstructure Evolution at Ni/Fe Interface in Dissimilar Metal Weld between Ferritic Steel and Austenitic Stainless Steel

Microstructural evolution of a low-alloy steel / nickel superalloy dissimilar metal weld during post-weld heat treatment

Localized Depth of Galvanic Corrosion at Dissimilar Metal Welding A508/Inconel 182/316L

Fine structure characterization of an explosively-welded GH3535/316H bimetallic plate interface

GTAW Dissimilar Weldment of sDSS 2507 and Nickel Alloy for Marine Applications: Microstructure–Mechanical Integrity

Microstructure and Mechanical Properties of MIG Welds between 6252 Armor Steel and Q550D HSLA Steel

Analysis of Stress Corrosion Cracking Growth Rate in the Heat-Affected Zone of 316L Based on the Heterogeneity of the Mechanical Properties

Microstructure and Properties of ZGMn13Mo/A514 Dissimilar Steel Multi-pass Welding

Microstructural Analysis of Partially Diluted Zones in Dissimilar Cladding: EBSD Insights on AWS E 309L Alloy via MIG Process in Single- and Double-Layer Depositions on ASTM A36 Steel

Insights into microstructure evolution and fracture mechanisms of welded joints of high strength steel patchwork components

Experimental Investigation On The Microstructure And Mechanical Properties Of Dss2205 And Ss304L Dissimilar Weldments

Studies on residual stresses and structural integrity of the dissimilar gas tungsten arc welded joint of sDSS 2507/Inconel 625 for marine application

Welding Process Optimization for Steam Generator Divider Plate Against Disbonding of Dissimilar Metal Weld

On the investigation of microstructure and mechanical properties of the AlCoCrFeNi 2.1 /316 L dissimilar spot-welded joint

Dissimilar joining of duplex AISI 2304 stainless steel/austenitic AISI 321 stainless steel using resistance spot welding technique: Microstructural evolutions, tensile-shear properties, and fracture analysis

Microstructure and Performance of Hybrid Laser-Arc Welded 40 Mm Thick 316 L Steel Plates

Investigation of microstructure and mechanical properties in dissimilar-metal welding between ferritic stainless steel and Co-based superalloy using electron beam welding

Evolution mechanism of interfacial microstructure and its effect on failure in dissimilar metal welds containing ferritic heat resistant steels