Abstract:The effect of rolling temperature on the incomplete recrystallization behavior and the relationship to mechanical properties in 0.06C–4Mn-1.2Cr (wt.%) steel was investigated. Three plates of experimental steel were produced by hot rolling at different temperatures and intercritical annealing processes in this study. The microstructure of experimental steels was examined by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The mechanical properties of test steel were examined by impact test and tensile test. Austenite reversion and cementite precipitation-dissolution was numerically simulated under the assumption of local equilibrium. With the decrease of hot rolling temperature from 1000 °C to 800 °C, the uniform equiaxed prior austenite grains microstructures changed to heterogeneous microstructures of laminated and ultrafine prior austenite grains arranged alternatively. The tensile and impact tests revealed that the medium manganese steels rolling at 800 °C had an excellent combination of mechanical properties. Elongation had a great relationship with retained austenite fraction and stability. The fractography of impact specimens was examined to explore the toughening mechanism of the micro-laminated steels. The steel with uniform equiaxed grain structure exhibited a relatively low tensile strength of 750 MPa and low elongation of ∼20% and an extremely poor low-temperature toughness of ∼40 J at −40 °C. An enhanced low-temperature toughness (∼233 J at −40 °C), as well as an improved tensile strength (823 MPa) and higher elongation of ∼40%, was obtained in the steel with heterogeneous microstructures. The content of austenite in heterogeneous microstructure is twice that in uniform equiaxed grain structure. And cementite dissolved more thoroughly in the heterogeneous microstructure. The high austenite content of heterogeneous microstructures enabled the steel to be significantly stronger and ductile, which contributed to the high tensile strength and elongation to some extent. It is concluded that the effect of interface decohesion resulted in the occurrence of delamination. And the high austenite content and delamination greatly improved the low-temperature toughness of experimental steel.

Microstructure and Mechanical Properties of Hot-Rolled Medium-Mn Steel Containing 3% Aluminum

Microstructure and Mechanical Properties of Medium Mn Steel Containing 3%al Processed by Warm Rolling

Microstructure and Mechanical Properties of a Novel Cold Rolled Medium-Mn Steel with Superior Strength and Ductility

Effect of intercritical annealing temperature on microstructure and mechanical properties of V-Ti-Mo microalloyed medium Mn steel

Influence of Aluminum on Microstructure and Mechanical Properties of Air‐Hardened Medium Manganese Steel

Influence of Intercritical Annealing on Microstructure, Ductility, and Toughness of Medium Mn Steels

Characterization of Microstructures and Mechanical Properties of Cold-Rolled Medium-Mn Steels with Different Annealing Processes

Tailoring retained austenite and mechanical property improvement in Al–Si–V containing medium Mn steel via direct intercritical rolling

Intercritically Annealed Medium-Manganese Steel: Insights into Microstructural and Microtextural Evolution, Strain Distribution, and Grain Boundary Characteristics

Analysis of the Relationship Between Microstructure and Mechanical Properties of Intercritically Annealed 3.5mn Steel

Heat Treatment Effects on the Microstructure and Mechanical Properties of a Medium Manganese Steel (0.2C–5mn)

Microstructural characteristics and tensile behavior of medium manganese steels with different manganese additions

Effect of rolling temperature on microstructure and mechanical properties of medium manganese steel

The impact of intercritical annealing temperature on microstructure and mechanical properties of an ultra-low carbon medium manganese heavy steel plates

Microstructural Evolution and Mechanical Properties of V-Containing Medium-Mn Steel Adopting Simple Intercritical Annealing

Ultra-Fine Heterogeneous Microstructure Enables High Strength-Ductility in a Cold-Rolled Medium Mn Steel

Effect of C and Mn element partitioning behavior on microstructure and properties of cold-rolled medium manganese TRIP steel

Roles of Al in Enhancing the Thermal Stability of Reverted Austenite and Mechanical Properties of a Medium-Mn TRIP Steel Containing 2.7 Mn

Effect of annealing temperature on microstructure and mechanical properties of rolled Mg-1Li-3Al-1Zn-0. 3( Al5Ti1B) alloy

Microstructure and Mechanical Property Development in a Hot-rolled and Annealed Mg-5Li-1Al Alloy Sheet

High strength and ductility combination in nano-/ultrafine-grained medium-Mn steel by tuning the stability of reverted austenite involving intercritical annealing