Abstract:We successfully synthesized Cu@Ag NPs paste, and they were successfully applied for joining Cu/Cu@Ag NPs paste/Cu firstly in air by the ultrasonic-assisted sintering (UAS) at a temperature of as low as 160 degrees C. Their sintered microstructures featuring with dense and crystallized phases are completely different with the traditional thermo-compression sintering. The shear strength of the joints reached to 54.27 MPa, exhibiting one order of magnitude higher than thermocompression sintering (TCS) at the same temperature (180 degrees C). This ultra-low sintering temperature and high performance of the sintered joints were ascribed to ultrasonic effects and systematically investigated. The ultrasonic vibrations had distinct effects on the metallurgical reactions of the joints, resulting in the contact and growth of Cu core and the stripping and connection of Ag shell, which contributes to the high shear strength. For the TCS, the sintering process can be characterized by two stages. Stage I includes the neck formation and growth among Ag layers through surface diffusion. This initial sintering of NPs does not require much thermal activation, so it can be obtained at a low temperature with weak bonding and the sintering rate is very low because of thinner Ag shells on Cu@Ag NPs. With the increase of temperature, part of core-shell nanoparticles would loss the shell and the Cu cores with fresh surfaces would be exposed and contact with others, leading to the occurrence of the Cu NPs sintering, which would step into the Stage II. Because of lower input energy, this Cu NPs sintering took place very limit. However, regarding to the UAS, due to overwhelming effects caused by the application of ultrasonic, the "dewetting" of Ag shells appears since the sharp increase of temperature, resulting in that the sintering process quickly reaches to the stage II. In this stage, the thin Ag shells shrink into tiny nodules on the Cu core surface, leading to fast sintering of the NPs. Because the tiny Ag nodules have extremely large surface to volume ratio, the starting temperature of sintering dramatically decreases based on the thermodynamic theory. Such low temperature sintering in air of Cu@Ag NPs to form die attachments with robust performances can be successfully applied in the fields of high power, auto electronics and harsh environmental device packaging.

Facile preparation of sintered Cu-Ag bimetallic nanoparticle paste with low porosity

A Novel Cu@Ag Nano Paste with Low Porosity for Rapidly Sintering in Air Condition

Low Temperature Bonding of Cu Metal through Sintering of AgNanoparticles for High Temperature Electronic Application

Study on the Sintering Characteristics and Application in Cu Bulk Bonding of Ag-nanoparticle Paste

Sintering Mechanism of the Cu–Ag Core–shell Nanoparticle Paste at Low Temperature in Ambient Air

Low Temperature Bonding Process Using Mixed Cu-Ag Nanoparticles for Electronic Packaging

The Synthesis of Cu-Ag Core-Shell Bimetallic Nanoparticles for IC Bonding

Novel Cu@Ag Micro/Nanoparticle Hybrid Paste and Its Rapid Sintering Technique via Electromagnetic Induction for High-Power Electronics

Ambient Aqueous-Phase Synthesis of Copper Nanoparticles and Nanopastes with Low-Temperature Sintering and Ultra-High Bonding Abilities

Synthesis of Ultra-Thin Cu/Ag Bimetallic Nanosheets Assisted by Polyvinylpyrrolidone As Template

Ultra-low Temperature Sintering of Cu@Ag Core-Shell Nanoparticle Paste by Ultrasonic in Air for High-Temperature Power Device Packaging.

Synthesis and Characterization of Highly-Dispersed Copper Submicron Particles for Low Temperature Sintering Joints

Mechanism of Ultrasonic-Assisted Sintering of Cu@Ag NPs Paste in air for High-Temperature Power Device Packaging

Synthesis with Glucose Reduction Method and Low Temperature Sintering of Ag-Cu Alloy Nanoparticle Pastes for Electronic Packaging

Preparation and Sintering Properties of Ag27Cu2Sn Nanopaste As Die Attach Material

Fabrication of Cu Particles with Porous Surface and Enhanced Sinter-Bondability between Cu Finishes by Physically In Situ Formation of Cu Nanoparticles Using Them

A mild aqueous synthesis of ligand-free copper nanoparticles for low temperature sintering nanopastes with nickel salt assistance

Ag-Sn Bimetallic Nanoparticles Paste for High Temperature Service in Power Devices

Novel Cu–Ag bimetallic porous nanomembrane prepared from a multi-component metallic glass

Preparation of Nanoparticle and Nanowire Mixed Pastes and Their Low Temperature Sintering

Fabrication Of A Hybrid Paste Consisting Of Microscale Ag-Plated Cu Flakes And Nanoscale Ag Particles And Characterization Of Low-Temperature Sintered Hybrid Paste Joints