Abstract:In response to rising CO2 emissions in the cement industry and the growing demand for durable offshore engineering materials, calcium sulphoaluminate (CSA) cement concrete, known for its lower carbon footprint and enhanced corrosion resistance compared to Ordinary Portland Cement (OPC), is increasingly important. However, the chloride transport behavior of CSA concrete in both laboratory and marine environments remains underexplored and controversial. Accordingly, the chloride ion transport behaviors and mechanisms of CSA concrete in laboratory-accelerated drying-wetting cyclic environments using NaCl solution and seawater, as well as in marine tidal environments, were characterized using the rapid chloride test (RCT), X-ray diffraction (XRD), mercury infiltration porosimetry (MIP), and thermogravimetric analysis (TGA). The results reveal that CSA concrete accumulates more chloride ions in NaCl solution than in seawater, with concentrations 2–3.5 times higher at the same water–cement ratio. Microscopic analysis indicates that calcium and sulfate ions present in seawater facilitate the regeneration of ettringite, thereby increasing the density of the surface pore structure. The hydration and repair mechanisms of CSA concrete under laboratory conditions closely resemble those in marine tidal conditions when exposed to seawater. Additionally, this study found that lower chloride ion concentrations and pH levels inhibit the formation of Friedel's salt. Therefore, laboratory experiments with seawater can effectively simulate CSA concrete's chloride transport properties in marine tidal environments, whereas NaCl solution does not accurately reflect actual marine conditions.

Chloride Distribution Feature in Surface Layer of Cement Paste under Cyclic Drying-Wetting Condition

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments

Influence of Carbonation on “maximum Phenomenon” in Surface Layer of Specimens Subjected to Cyclic Drying-Wetting Condition

Chloride Ion Ingress Distribution Within an Alternate Wetting-Drying Marine Environment Area

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Influence of evaporation rate on pore size distribution, water loss, and early-age drying shrinkage of cement paste after the initial setting

Chloride penetration in concrete exposed to cyclic drying-wetting and carbonation

Study On Relationship Between Chloride Diffusion In Concrete And Time

Chloride Penetrating under Co-Effects of Initial Curing and Exposure Conditions

EXPERIMENTAL STUDY ON THE CHLORIDE DIFFUSION OF CONCRETE BASED ON ITS PORE STRUCTURE

Influence of moisture condition on chloride diffusion in partially saturated ordinary Portland cement mortar

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Chloride Ion Distribution in Concrete of Dry-Wet Cycling Region along Elevated Altitude

MECHANISM AND MATHEMATIC MODELING OF CHLORIDE PERMEATION IN CONCRETE UNDER UNSATURATED STATE

Development of cementitious capillary crystalline waterproofing agents and durability study of concrete in the presence of chloride with sulfate in aqueous environment

Chloride Binding Capacity and Its Effect on the Microstructure of Mortar Made with Marine Sand

Drying–Wetting Correlation Analysis of Chloride Transport Behavior and Mechanism in Calcium Sulphoaluminate Cement Concrete

Experimental analysis on the relationship between pore structure and capillary water absorption characteristics of cement‐based materials

Co-effects of initial and exposure environments on chloride penetration

Chloride binding to calcium silicate hydrates (C-S-H) in cement paste: a molecular dynamics analysis