Abstract:Abstract Substantial research effort has been devoted on linking corrosion-induced cracking of concrete with the internal corrosion damage level. Still, numerical models of the corrosion and cracking process require internal parameters, that cannot be directly evaluated from experimental data. Therefore, this study provides a novel experimental method for monitoring the effects of steel corrosion adjacent to the steel-concrete interface. This non-destructive method is suited for small-scale laboratory-made specimen, and was designed to provide missing information required for subsequent calibration of numerical models. Hollow steel bars were cast into concrete and subjected to accelerated corrosion using the impressed current technique. The deformations of the hollow steel bars were measured using distributed strain sensing in an optical fibre, attached to the inner surface of the hollow steel bars. After the corrosion period, X-ray Computed Tomography scans were performed to evaluate concrete cracking and corrosion level. The results reveal a non-uniform distribution of strain around the perimeter of the steel, indicating a non-uniform radial stress distribution. The non-uniformity correlated very well with the position of the corrosion-induced cracks; with extension hoop strains in the steel at the location of these cracks and contraction hoop strains in between. Further, the corrosion level varied around the perimeter, with higher values near cracks. The combination of non-destructive monitoring techniques used in this study on small-scale laboratory-made specimens show great potential to reveal new insights on how the corrosion pattern, corrosion-induced cracking of the concrete cover and stress (indirectly measured through the strain in the steel) interact throughout the corrosion process.

Stress Corrosion Cracks: Through-Wall Transmission Measurements In 510 Mm Steel Pipe

Study on Measurement Method of Interior Stress Distributions in Engineering Rolled-Plates

Corrosion-Induced Cracking Propagation Of Rc Beams Subjected To Different Corrosion Methods And Load Levels

Peridynamic Investigation of Stress Corrosion Cracking in Carbon Steel Pipes

Crack Propagation and Flexural Behaviour of Rc Beams under Simultaneous Sustained Loading and Steel Corrosion

Observations of Stress Corrosion Cracking in Pipeline Steel in Corrosive Seawater Environment Including Detailed Observation of the Crack Initiation Mechanism

Initiation of Stress Corrosion Cracks in X80 and X100 Pipe Steels in Near-Neutral Ph Environment

Microstructural Effects in the Development of Near-Neutral pH Stress Corrosion Cracks in Pipelines

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Characteristic of Acoustic Emission Signal from Stress Corrosion Cracking in Low-Carbon Nitrogen-Enhanced Stainless Steel

Characterization of Magnetic Field in Crack Propagation Stage and Application to Non-Destructive Evaluation

Study of Stress-Corrosion Cracking on 304 Stainless Steel by Wedge Opening Loading Method and Acoustic Emission Technique

Study on Stress Corrosion Cracking Behavior of Incoloy825/X65 Bimetallic Composite Pipe Welded Joint in Wet Hydrogen Sulfide Environment

Reconstruction of Stress Corrosion Cracks Based on Pulsed Eddy Current Signals

An Investigation of Corrosion-Induced Stress During SCC

Stress Corrosion Cracking at Low Loads: Surface Slip and Crystallographic Analysis

Electrochemical and Stress Corrosion Mechanism of Submarine Pipeline in Simulated Seawater in Presence of Different Alternating Current Densities

Surface Stress Analysis of Internally Corroded Pipes under External Pressure

Finite-Element Calculations of Remote Field Eddy Current Interactions with Slit Defects

Stress corrosion cracking behavior of X80 pipeline steel under alternating current, Desulfovibrio desulfurican and cathodic protection potential

Monitoring corrosion-induced concrete cracking adjacent to the steel-concrete interface