Abstract:The microstructure evolution and mechanical properties of biodegradable Mg–3Sn–1Zn–0.5Mn alloys were investigated by the optical microscopy, X-ray diffractometer and a universal material testing machine.The corrosion and degradation behaviors were studied by potentiodynamic polarization method and immersion test in a simulated body fluid（SBF）. It was found that the as-extruded Mg–3Sn–1Zn–0.5Mn alloy has the fine equiaxed grains which underwent complete dynamic recrystallization during the hot extrusion process, with the second phase particles of Mg 2 Sn precipitated on the grain boundaries and inside the grains. The tensile strength and elongation of as-extruded Mg–3Sn–1Zn–0.5Mn alloys were 244 ± 3.7 MPa and 19.3% ± 1.7%, respectively. The potentiodynamic polarization curves in SBF solution indicated the better corrosion resistance of the as-extruded Mg–3Sn–1Zn–0.5Mn alloy in the SBF solution. Immersion test in the SBF solution for 720 h revealed that the corrosion rate of as-extruded Mg–3Sn–1Zn–0.5Mn alloy was nearly 4 ± 0.33 mm/year. The hemolysis rate of as-extruded Mg–3Sn–1Zn–0.5Mn alloy was lower than the safe value of 5% according to ISO 10993-4. As-extruded Mg–3Sn–1Zn–0.5Mn alloy showed good biocompatibility after being implanted into the dorsal muscle and the femoral shaft of the rabbit, and no abnormalities were found after short-term implantation. It was revealed that the as-extruded Mg–3Sn–1Zn–0.5Mn alloy is a promising material for biodegradable implants,which possesses an interesting combination of preferred mechanical properties, better corrosion resistance and biocompatibility.

Development of High Performance Mgfe Alloy As Potential Biodegradable Materials

Preparation of Biodegradable Mg-Fe Alloy with High Strength and Excellent Ductility Via Spark Plasma Sintering Process

Microstructure, Mechanical Properties, and in Vitro Corrosion Behavior of Biodegradable Zn-1Fe-xMg Alloy

Development of Fe-Mg alloys with intermediate degradation kinetics as potential biodegradable bone implants

Design of Fe–Mn–Ag Alloys As Potential Candidates for Biodegradable Metals

Development and Prospects of Biodegradable Magnesium Alloys

Advances in Fe-based Biodegradable Metallic Materials

Mechanical and Corrosion Properties of Mg-Gd-Zn-Zr-Mn Biodegradable Alloy by Hot Extrusion

Microstructure Evolution in Mg-Zn-Zr-Gd Biodegradable Alloy: the Decisive Bridge Between Extrusion Temperature and Performance

Recent advances on the development of magnesium alloys for biodegradable implants

Microstructure, Mechanical Properties and in Vitro Degradation Behavior of Novel Zn-Cu-Fe Alloys

In Vitro Study on Mg-Sn-Mn Alloy As Biodegradable Metals

Research on an Mg-Zn alloy as a degradable biomaterial.

A review on magnesium alloys as biodegradable materials

Systems, Properties, Surface Modification and Applications of Biodegradable Magnesium-Based Alloys: A Review

Research Progress on the Alloying of Biodegradable Magnesium Alloys

In Vitro Investigation of Fe30Mn6Si Shape Memory Alloy As Potential Biodegradable Metallic Material

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Enhanced Mechanical Performance of a Biodegradable Fe-Mn Alloy Manufactured by Metal Injection Molding and Minor Carbon Addition

In Vitro and in Vivo Studies on A Mg-Li-X Alloy System Developed As A New Kind of Biological Metal