Abstract:Mg-1.5Y-1.2Zn-0.44Zr alloys were newly developed as degradable metallic biomaterials. A comprehensive investigation of the microstructure, mechanical properties, in vitro degradation assessments and in vitro cytotoxicity evaluations of the as-cast state, as-heat treated state and as-extruded state alloys was done. The microstructure observations show that the Mg-1.5Y-1.2Zn-0.44Zr alloys are mainly composed of the matrix α-Mg phases and the Mg12ZnY secondary phases (LPS structure). The hot extrusion method significantly refined the grains and eliminated the defects of both as-cast and heat treated alloys and thereby contributed to the better mechanical properties and biodegradation resistance. The values of tensile strength and tensile yield strength of the alloy in the as-extruded condition are about 236 and 178 MPa respectively, with an excellent elongation of 28%. Meanwhile, the value of compressive strength is about 471 MPa and the value of bending strength is about 501 MPa. The superior bending strength further demonstrates the excellent ductility of the hot extruded alloys. The results of immersion tests and electrochemical measurements in the SBF indicate that a protective film precipitated on the alloy's surface with the extension of degradation. The protective film contains Mg(OH)2 and hydroxyapatite (HA) which can reinforce osteoblast activity and promote good biocompatibility. No significant cytotoxicity towards L-929 cells was detected and the immersion extracts of alloy samples could enhance the cell proliferation with time in the cytotoxicity evaluations, implying that the Mg-1.5Y-1.2Zn-0.44Zr alloys have the potential to be used for biomedical applications.

In Vitro Investigation of Fe30Mn6Si Shape Memory Alloy As Potential Biodegradable Metallic Material

FeMnCSi alloy for degradable pin implants: surface and in vitro characterization

Microstructure, Mechanical Properties and in Vitro Degradation Behavior of Novel Zn-Cu-Fe Alloys

In Vitro Study on Mg-Sn-Mn Alloy As Biodegradable Metals

Microstructure, Mechanical Properties, and in Vitro Corrosion Behavior of Biodegradable Zn-1Fe-xMg Alloy

In Vitro Study on Mg e Sn e Mn Alloy as Biodegradable Metals

Preparation of Biodegradable Mg-Fe Alloy with High Strength and Excellent Ductility Via Spark Plasma Sintering Process

Investigations on the Degradation Behavior of Processed FeMnSi-xCu Shape Memory Alloys

In Vitro Corrosion Behavior of Zn3Mg0.7Y Biodegradable Alloy in Simulated Body Fluid (SBF)

Design and characterizations of novel biodegradable Zn-Cu-Mg alloys for potential biodegradable implants

Effect of grain size on the mechanical properties of Fe-30Mn-6Si biodegradable alloy

Microstructural, mechanical, corrosion and cytotoxicity characterization of the hot forged FeMn30(wt.%) alloy

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Development of High Performance Mgfe Alloy As Potential Biodegradable Materials

Micro-alloying with Mn in Zn–Mg alloy for future biodegradable metals application

Enhanced Mechanical Performance of a Biodegradable Fe-Mn Alloy Manufactured by Metal Injection Molding and Minor Carbon Addition

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity Evaluations of Mg–1.5Y–1.2Zn–0.44Zr Alloys for Biodegradable Metallic Implants

Fabrication and Properties of Zn-3Mg-1Ti Alloy as a Potential Biodegradable Implant Material

Comparative In Vitro Study of Ti-12V-9Sn Shape Memory Alloy with C.P. Ti and Ti-12V Alloy for Potential Biomedical Application

In vitro degradation behavior of Fe-20 Mn-1.2C alloy in three different pseudo-physiological solutions

Microstructure, mechanical properties, in vitro degradation behavior and hemocompatibility of novel Zn–Mg–Sr alloys as biodegradable metals