Thermal effects on the fracture of adhesively bonded composite-concrete interface

Pizhong Qiao,Yingwu Xu
2005-01-01
Abstract:A test method using a notched three-point bending beam (3PBB) specimen is presented to characterize the thermal effects on the Mode-I fracture of composite-concrete bonded interfaces. The interface fracture energy under various temperatures is evaluated based on a fictitious crack model. A common epoxy resin system is used to impregnate carbon fiber fabrics and then bond the carbon fiber-reinforced polymer (CFRP) composite to the concrete. Mode-I fracture tests of the 3PBB specimens for CFRP-concrete bonded interfaces are performed to determine the applied load and load point displacement relationship, from which the interface fracture energy is computed. A temperature range from -34.4 degrees C (-30 degrees F) to 71.1 degrees C (160 degrees F) with about 16.67 degrees C (30 degrees F) increments is applied to the fracture tests, and the effect of temperature on the fracture energy of CFRP-concrete bonded interfaces is studied and discussed. The results indicate that the thermal effects are pronounced on the properties (e.g., the interface fracture energy, critical load, and fractured surface) of adhesively bonded composite-concrete interfaces. The test data presented are useful for design of concrete structures externally reinforced with FRP composites, and the test protocol of modified 3PBB specimens can be used as a qualification method to test new hybrid material interface bonds and to study durability-related effects on the interface.
What problem does this paper attempt to address?