Abstract:Ultrahigh-toughness cementitious composite (UHTCC) is a new type of cementitious material that is suitable for durability repair of deteriorated concrete structures. One of the key issues in this repair technology is the behavior of interfacial bonds. In this study, the bond properties between the UHTCC and the old concrete were evaluated by conducting four-point bending tests. The UHTCC was prepared using two methods: cast-in-situ and prefabrication. The test parameters include the roughness of the concrete substrate, roughness of the prefabricated UHTCC, strength of the old concrete, primer, and bonding agent. Two-way analysis of variance was used to analyze the effect of these test parameters on the bond strength. Moreover, two regression formulae were proposed to predict the flexural bond strength of the composite beams. The results showed that the flexural bond strength of the repair system tended to increase with the increase in the roughness values of the concrete substrate and prefabricated UHTCC and strength of the old concrete. However, a very high roughness could damage the interfacial zone; hence, the roughness should be controlled in a particular range. The results also revealed that suitable primers and bonding agents, e.g.,polymer-modified material and fly ash-silica fume-modified material, could improve the bond strength of the interface. Moreover, double-layer bonding configurations were found to exist in the prefabricated repair system. The flexural bond strength depends on the weaker bonding plane, and the interface control needs to be considered during the design and construction. In particular, two-way analysis of variance was proven a reliable tool in evaluating the experimental results. The predicted flexural bond strength was in good agreement with the experimental value.

Experimental study on fracture behavior of UHTCC overlay/concrete interfaces under mixed-mode loading

Evaluation of the Fracture Properties of the Bond Interfaces Between UHTCC Overlays and Concrete Substrates

STUDY ON FRACTURE PROCESS OF CONCRETE THREE-POINT BENDING BEAMS RETROFITTED WITH UHTCC

Experimental study on the flexural performance of concrete beam strengthened with ultra high toughness cementitious composites

Shear Fracture Performance of the Interface Between Ultra-High Toughness Cementitious Composites and Reactive Powder Concrete

Comparison of Cast-In-Situ and Prefabricated UHTCC Repair Systems under Bending

Flexural and Interface Behaviors of Reinforced Concrete/Ultra-High Toughness Cementitious Composite (rc/uhtcc) Beams

Experimental study on flexural fatigue property of existing concrete beams restricted by post-poured UHTCC layer

Four Point Bending Experimental Investigation on Reinforced Ultra High Toughness Cementitious Composite Beams

Experimental Investigation and Analysis on Flexural Performance of Functionally Graded Composite Beam Crack-Controlled by Ultrahigh Toughness Cementitious Composites

Flexural Behaviors of Rc Beams Strengthened with Post-Poured Uhtcc Layer

Improvement of the flexural and cracking behavior of RC beams using ultra-high toughness cementitious composites(I):theoretical analysis

Fracturing behaviors of FRP-strengthened concrete structures

Experimental Study On Flexural Fatigue Property Of Ultra-High Toughness Cementitious Composites

A Design Concept with the Use of Ruhtcc Beam to Improve Crack Control and Durability of Concrete Structures

Experimental study on fracture evaluation criterion of ultra-high toughness cementitious composites

Fatigue Performance of Prefabricated Composite T‐beams under Cyclic Overloading: an Experimental Study

Improvement on flexural and cracking behavior of RC beam using ultra-high toughness cementitious composite Ⅱ: experimental study

DURABILITY PERFORMANCE OF RUHTCC BEAM UNDER FLEXURAL LOAD

Monotonic and Fatigue Performance in Bending of Fiber-Reinforced Engineered Cementitious Composite in Overlay System

Flexural Crack Control Performance of Existing Concrete Composite Beam Reinforced by Post-poured UHTCC