Abstract:With green and low-carbon developments in oil fields, an increasing amount of repaired oil tubing is being used as oil and gas transmission pipelines in China. However, due to differences in manufacturing standards between oil tubing and transmission pipelines, there are inevitably some issues during their use. This paper investigates a case of cracking failure in repaired oil tubing used as a gathering and transportation pipeline. The failure occurred after eight months of operation and was characterized by a circumferential crack at the male thread end of the tubing joint. To determine the root cause of the failure, a series of experiments were conducted on the oil tubing. The experiments included visual inspection, chemical composition analysis, mechanical properties testing, hardness testing, metallographic examination, and microstructure analysis. The results revealed that the thread of the cracked tubing was not tightened to the specified position; the connection between the tubing and the coupling was welded in a circumferential direction; and cracks occurred in the heat-affected zone of the weld. Chemical composition, tensile performance, and the Charpy impact of the tubing meet the requirements of API 5CT for P110 material, and no abnormalities were found in the metallographic structure. The microstructure at the weld toe of the fracture is martensite, and the hardness is 476 HV10. Based on the thermal simulation verification test, when the material of the tubing cools from 1200 °C, which is located in the coarse HAZ temperature zone, the base metal transforms into martensite with a little granular bainite, exhibiting its highest hardness value at 371 HV10, which is higher than the allowable hardness for carbon steel and indicates the material has poor weldability. The reasons for the cracking and failure of the tubing are that the P110 repaired tubing has a high carbon equivalent and poor weldability. During the welding process, martensitic structure was formed at the weld toe, and cold cracks appeared in the heat-affected zone, resulting in failure. To avoid the reoccurrence of such failure, recommendations are proposed.

Investigation of the Root Cracking of SA335 P91 Steel Welded Joint

Effect of Welding Parameters on Solidification Cracking in Butt Weld Roots of SA335 P91 Pipes

Cause Analyses of the Weld Seam Cracks of a Prehydrogenating Reactor

Cracking Causes of Welded Joint of T91 Steel Steam Sampling Tube in Ultra Supercritical Unit Boiler

Cause Analysis and Preventive Measures against Cracks in 15Cr1Mo1V Steel Welded Joint in Service

Analysis of weld root fatigue cracking in load-carrying high-strength aluminum alloy cruciform joints

Cause Analysis and Improvement Measures for Pipeline Cracking of 9Cr-1Mo Material

Failure Analysis of Cracked P110 Repaired Tubing Used for Gas Transmission

Cracking Reason Analysis on Circumferential Welding Joints of F52 Flange and X52 Welded Pipe Butt Welding

3D finite element simulation on stress-strain distributions in all position root butt welding of pip

Studies on Mechanism of Zigzag Crack Forming Process in Weld Metal of Narrow Gap Submerged Arc Welding of Thick Plate

The Effect of Pipeline Root Weld Microstructure on Crack Growth Behaviour

Strain Visualization of Growing Short Fatigue Cracks in the Heat-Affected Zone of a Ni–Cr–Mo–V Steel Welded Joint: Intergranular Cracking and Crack Closure

Root Cause Analysis for Cracked Pipe in Auxiliary System in Nuclear Power Plant

Failure Analysis of Weld Cracking in a Thick-Walled 2.25Cr-1Mo Steel Pressure Vessel

Analysis on Weld Cracking in Q345 Cylinder

Investigation of Early Cracking of Dissimilar Metal Welds in a 1000-MW Ultra-supercritical Power Plant Close to the Sea

Analysis of Surface Cracks on TP347H Stainless Steel Tube

Research on the Cold Crack Sentivity of P92 Steel and Its Welding Material

Analysis for a crack of the manhole in a reactor of Ethidene Diamine unit

Analysis and Research on Crack Failure of P91 Pipe