Analysis of weld root fatigue cracking in load-carrying high-strength aluminum alloy cruciform joints

Ping Wang,Xianjun Pei,Pingsha Dong,Yifei Yu,Xiangwei Li

DOI: https://doi.org/10.1016/j.ijfatigue.2020.105735

IF: 5.489

2020-10-01

International Journal of Fatigue

Abstract:<p>This study presents experimental and analytical investigation into weld root cracking behaviors in load-carrying high-strength aluminum alloy cruciform joints. In the experiment, electric spark machining cutting was used to control weld penetration consistency. An analytical weld root stress model is proposed for establishing governing parameter controlling weld root failure and predicting failure plane angle. Its lower-order form in terms of nominal stress is also proven to be adequate for interpreting test data, which is much simpler for practical application. Comparison between the lower-order weld root traction stress and "engineering shear stress" used in some Codes and Standards are also discussed.</p>

materials science, multidisciplinary,engineering, mechanical

What problem does this paper attempt to address?

The paper attempts to address the issue of the mechanism and influencing factors of fatigue crack initiation at the weld root in high-strength aluminum alloy cruciform joints under load. Specifically, the researchers explored the following issues through experimental and analytical methods:

1. **Generation of fatigue cracks at the weld root**: The researchers tried to understand how fatigue cracks at the weld root are generated in high-strength aluminum alloy cruciform joints through experimental observation and analysis.

2. **Establishment of control parameters**: An analytical weld root traction stress model was proposed to determine the key parameters controlling weld root failure and to predict the angle of the failure plane.

3. **Data correlation**: The effectiveness of the proposed equivalent weld root stress parameter in explaining experimental data was verified, particularly its simplicity and accuracy in practical applications.

4. **Comparison of different fatigue assessment methods**: The proposed low-order weld root traction stress was compared and discussed with the "engineering shear stress" used in some standards and codes to evaluate its applicability under different loading conditions and joint geometries.

Overall, the paper aims to deeply understand the behavior of fatigue cracks at the weld root through experimental and theoretical analysis, and to provide a scientific basis for the design and evaluation of welded joints in high-strength aluminum alloy structures.