Effect of calcium titanate addition on properties of MgO-CaO materials
Mingjie Han,Ling Zhang,Jian Yang,Yang Gao,Wenkai Liu
DOI: https://doi.org/10.3969/j.issn.1001-1935.2016.03.013
2016-01-01
Refractories
Abstract:In order to prolong the service life of MgO-CaO bricks for AOD furnace,the columnar specimens (φ50 mm ×55 mm)were prepared using magnesia-calcium oxide sand and fine (CaO 20 mass%,8-5, 5 -2,2-0,≤0.074 mm)as the main raw materials,paraffin as the binder,adding calcium titanate fines (CaTiO3 93 mass%,≤0.074 mm)with different additions (0,2%,4%,6%,8%,10%,12%,14%,by mass),mixing,pressing in a hydraulic press under 450 MPa,and then firing at 1 500 ℃for 2 h.The appar-ent porosity,bulk density,linear change on heating,thermal shock resistance and slag resistance were re-searched.The results show that with calcium titanate fine addition increasing,the density,linear shrinkage rate,cold crushing strength and thermal shock resistance firstly increase and then decrease,and the inflec-tion point is at 8% calcium titanate fine;the specimens perform the best slag resistance when adding 6%and 8% calcium titanate.