Abstract:Abstract Mullite porous ceramics with high porosity and good mechanical properties were prepared by foaming method combined with gel casting process using kaolin and alumina as main raw materials and sodium polyoxyethylene ether sulfate as foaming agent. The effects of sintering process and magnesium oxide content on the microstructure and properties of mullite porous ceramics were investigated. The studies show that: With the addition of magnesium oxide, the amount of mullite produced and the compactness of the sample will increase. At this time, the microscopic morphology of mullite is needle-like and prismatic, and the mechanical properties are better. and the pore size distribution gradually tends to be between 0.1-0.2mm and 0.2-0.3mm. The addition of magnesium oxide, The amount of mullite phase increased, the densification degree of the sample increased, and the acicular and prismatic mullite phases with good mechanical properties were mainly formed, and the porosity of mullite porous ceramics decreased and the compressive strength increased. The pore size distribution gradually tends to be between 0.1-0.2mm and 0.2-0.3mm. As the sintering temperature increases, the porosity of mullite porous ceramics decreases and the compressive strength increases. With the extension of the holding time, the amount of mullite phase generated increases, the porosity remains basically unchanged, and the compressive strength increases.

Effect of Sintering Temperature on Mechanical Properties of Porous Silica Ceramic

The Effect of SiO2 Addition on Phase and Microstructure of Porous Silica Ceramic

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Effects of sintering temperature on properties of porous mullite/corundum ceramics

Sintering effects on the development of mechanical properties of fired clay ceramics

Effect Of Sintering Process On Micro-structure And Properties Of Mullite Porous Ceramics Containing magnesium oxide

INFLUENCE OF SINTERING PROCESS ON PROPERTY OF POROUS CERAMICS FROM QUARTZ SAND

Effects of Sintering Additives on Microstructure and Properties of Porous SiC Ceramics with High Porosity

Effect of Sintering Temperature on Properties of YAG Porous Ceramics via Atmospheric Sintering Method

Effect of sintering temperature on the phase, microstructural, physical, mechanical, and in vitro biomineralisation properties of porous wollastonite ceramics fabricated using the gel casting method

Effect of Sintering Temperature on the Structures and Properties of Porous Aluminium Titanate Ceramics

Effect of Sintering Temperature on Compressive Strength of Porous Yttria-Stabilized Zirconia Ceramics

Effect of Sintering Temperature on Properties of Porous SiC Ceramics Produced Through Coat-mix/Composite Additives Process

Effects of sintering temperature on properties of diatomite-based dental ceramic

A Simple and Efficient Way to Prepare Porous Mullite Matrix Ceramics Via Directly Sintering SiO2-Al2O3 Microspheres

Porous Silica Ceramics with Uniform Pores from the In-Situ Foaming Process of Silica Poly-Hollow Microspheres in Inert Atmosphere

Effect of BPO4-B2O3 Composite Additive on Crystallization and Sintering of Silica Ceramics

Effect of pore structure evolution on mechanical properties and thermal conductivity of porous SiC-Mullite ceramics

Effects of the Starting Powders on Microstructure and Properties of Porous Silica Ceramics

Improved precision and mechanical properties of 3D‐printed silica ceramics via sintering temperature optimization

Effect of Diatomite Additive on the Mechanical and Dielectric Properties of Porous SiO2-Si3N4 Composite Ceramics