Effects of Strontium on Microstructures of Hypereutectic Mg-Si Alloy

Peng GENG,Peipeng JIN,Mingliang WANG,Binbin TANG,Xi WANG

DOI: https://doi.org/10.16410/j.issn1000-8365.2015.02.047

2015-01-01

Abstract:The hypereutectic Mg-4%Si alloy was modified by adding Mg-25%Sr master alloy. The effect of Sr addition on the modification of the primary Mg2 Si phases and the modification mechanisms were investigated. The results show that the primary Mg2 Si phases were effectively modified by Sr addition. The size of the primary Mg2 Si phases was clearly decreased by Sr addition(average size from about 50 μm to about 20 μm), and the primary Mg2 Si phases change from coarser dendrites to finer dendrites, the shapes of the primary Mg2 Si particles from the irregular shapes to relatively regular shapes.The shapes of the eutectic Mg2 Si particles change from obvious Chinese characters shapes to fine short rod shapes. There are two modification mechanisms, First, more primary Mg2 Si growth due to Sr-rich particles as heterogeneous nucleation sites. Secondly, Sr enriched in growth surface of eutectic Mg2 Si phase inhibits the preferred growth manner of the eutectic.