Effects of Ca and Sr on Microstructure of AS21 Magnesium Alloy

王岩,戚文军,郑飞燕,翁康荣,赵红亮
2010-01-01
Abstract:The effects of Ca and Sr addition on microstructure of AS21 magnesium alloy were studied. The main phases in the AS21 alloy are α-Mg matrix,Mg2Si and a small amount of β-Mg17Al12 phase. Addition of Ca succeeded in transforming the Mg2Si phase from the present dendritic morphology into small and well-distributed round particles. The average size of Mg2Si phase was reduced from 47 μm to 6 μm with the optimal Ca addition of 0.25%. The distribution of Mg2Si was more dispersed and the average size was reduced to 4 μm after adding 0.1% Sr into AS21-0.25Ca. When the addition of Sr reached 0.3%,a new needle-like MgCaSi ternary phase was observed.