Abstract:The formation of solid calcium carbonate (CaCO3) from aqueous solutions or slurries containing calcium and carbon dioxide (CO2) is a complex process of considerable importance in the ecological, geochemical and biological areas. Moreover, the demand for powdered CaCO3 has increased considerably recently in various fields of industry. The aim of this study was therefore to synthesize fine particles of calcite with controlled morphology by hydrothermal carbonation of calcium hydroxide at high CO2 pressure (initial PCO2=55 bar) and at moderate and high temperature (30 and 90 degrees C). The morphology of precipitated particles was identified by transmission electron microscopy (TEM/EDS) and scanning electron microscopy (SEM/EDS). In addition, an X-ray diffraction analysis was performed to investigate the carbonation efficiency and purity of the solid product. Carbonation of dispersed calcium hydroxide in the presence of supercritical (PT=90 bar, T=90 degrees C) or gaseous (PT=55 bar, T=30 degrees C) CO2 led to the precipitation of sub-micrometric isolated particles (<1$\mu$m) and micrometric agglomerates (<5$\mu$m) of calcite. For this study, the carbonation efficiency (Ca(OH)2-CaCO3 conversion) was not significantly affected by PT conditions after 24 h of reaction. In contrast, the initial rate of calcium carbonate precipitation increased from 4.3 mol/h in the "90bar-90 degrees C" system to 15.9 mol/h in the "55bar-30 degrees C" system. The use of high CO2 pressure may therefore be desirable for increasing the production rate of CaCO3, carbonation efficiency and purity, to approximately 48 kg/m3h, 95% and 96.3%, respectively in this study. The dissipated heat for this exothermic reaction was estimated by calorimetry to be -32 kJ/mol in the "90bar-90 degrees C" system and -42 kJ/mol in the "55bar-30 degrees C" system.

Preparation of Super-fine Spherical CaCO3 by the Carbonation Method

Modulation of nano CaCO3pore size and effect on properties of carbonation reaction

Preparation of cage-like nano-CaCO3 hollow spheres for enhanced CO2 sorption

Preparation of Nano-CaCO3 from Phosphogypsum by Gas–Liquid–Solid Reaction for CO2 Sorption

Study on the kinetics of Ca-based CO2 sorbent of carbonation and calcination for adsorption enhanced reforming process

Preparation of MgO-coated Nano CaO Using Adsorption Phase Reaction Technique for CO2sorption

Optimization of Calcium Carbide Residue Utilization for Producing High‐quality Calcium Carbonate

Influence of chemical additives on the formation of super-fine calcium carbonate

Particle Carbonation Kinetics Models and Activation Methods under Mild Environment: the Case of Calcium Silicate

Preparation of ultrafine calcium carbonate particles with micropore dispersion method

New carbonation reactor for the preparation of sphere-like nano-calcium carbonate

Preparation of Ultrafine Caco3 with Different Morphologies by Controlled Precipitation Method

Lattice Boltzmann Simulation on Carbonation of CaO with CO2

Facile Preparation of Micro and Nano-Sized CaCO3 Particles by a New CO2-storage Material

Rhombohedral calcite precipitation from CO2-H2O-Ca(OH)2 slurry under supercritical and gas CO2 media

Preparation and In-Situ Surface Modification of CaCO3 Nanoparticles with Calcium Stearate in a Microreaction System

Experimental Study on Preparation of Calcium Oxide by Coal Reduction of Calcium Sulfate in Carbon Dioxide Atmosphere

Ultrahigh Purity CaCO3 Whiskers Derived from the Enhanced Diffusion of Carbonate Ions from a Larger Liquid–gas Interface Through Porous Quartz Stones

Preparation of Calcium Carbonate Nanoparticles from Waste Carbide Slag Based on CO2 Mineralization

Effect of Crystal Orientation Agents on Morphology of Nano-CaCO3

The Effect of Ultrasonic Field on Synthesis of Nanometer Calcium Carbonate and Its Growth Mechanism