Preparation of MgO-coated Nano CaO Using Adsorption Phase Reaction Technique for CO2sorption

Haoliang Ping,Yan Wang,Sufang Wu

DOI: https://doi.org/10.1039/c6ra05452h

IF: 4.036

2016-01-01

RSC Advances

Abstract:Preparation of MgO-coated nano CaO using adsorption phase reaction technique for CO2sorption.

What problem does this paper attempt to address?

Synthesis of a Porous Nano‐CaO/MgO‐Based CO2 Adsorbent

peiqiang lan,sufang wu

DOI: https://doi.org/10.1002/ceat.201300709

IF: 2.2148

2014-01-01

Chemical Engineering & Technology

Abstract:A porous nano-CaO/MgO-based adsorbent was prepared using MgO as a support in order to increase the sorption capacity and durability. The magnesium sol prepared by reacting MgO slurry with citric acid was added to nano-CaCO3 slurry and the mixture was calcinated to obtain the nano-CaO/MgO-based adsorbent. The influence of MgO content on the structure and sorption performance of the resulting adsorbent was studied in detail. The pore radius and specific surface area of the adsorbent increased with higher MgO content. The adsorbent exhibited superior sorption performance during calcium looping and maintained a good durability at the calcination temperature, thus being an interesting candidate for future work.
A new nano CaO-based CO2 adsorbent prepared using an adsorption phase technique

Yan Wang,Yanqing Zhu,Sufang Wu

DOI: https://doi.org/10.1016/j.cej.2012.11.095

IF: 15.1

2013-01-01

Chemical Engineering Journal

Abstract:This study describes for the first time micro-scale hydrolysis has been used in the adsorption phase to prepare a nano CaO-based CO2 adsorbent with a highly durable sorption capacity. The hydrolysis of Ti(OC4H9)4 to form TiO2 was used to prepare TiO2-coated nano CaCO3, which was then calcinated to prepare a nano CaO-based CO2 adsorbent with a controlled coating layer. The coating compactness was defined for the first time in this study to describe the mole ratio of Ti to Ca on the surface of the nano CaCO3. The coating compactness and the durability of the sorption capacity of samples with varying TiO2 content, hydrolysis temperature, and ester concentration were studied in detail. The properties of the reactive adsorption of the prepared nano CaO-based CO2 adsorbents were tested using a thermo-gravimetric analyzer. The results showed that, of the conditions tested, the TiO2 content exerts the most influence on the durability of the sorption capacity. The nano CaCO3 that was coated with 10 wt.% TiO2 and prepared under 20°C, which has a corresponding coating compactness of 1.0, exhibited a much more durable CO2 sorption capacity than the other prepared samples.
Adsorption Properties of Coating Modified Nano CaO-Based CO2 Adsorbents

Xiaochong Xue,Yan Wang,Sufang Wu

2015-01-01

Abstract:The adsorbent was prepared in a spray granulation method by mixing the inert material MgO or TiO2 coating modified with nano-CaCO3 and with alumina sol as binder. The thermo-gravimetric analyzer was used to investigate the decomposition temperature, adsorption rate, adsorption capacity and stability under the conditions of reactive carbonation temperature 600℃, CO2partial pressure 0.015 MPa,and calcination temperature 750℃ in nitrogen gas. The results showed that the decomposition temperature of MgO, TiO2 coating modified nano CaO-based CO2adsorbent was increased by 20 and 35℃, respectively. The adsorption rate and adsorption capacity were both higher than those of uncoated nano CaO-based CO2 adsorbent after 30 carbonation-calcination cycles. The TiO2 coated nano CaO-based CO2adsorbent had the highest stability with 34.85% decrement after 30 cycles, and the MgO coated one was 38.89% while the uncoated nano CaO-based CO2 adsorbent was 54.87%.
In Situ Preparation of CaTiO3 and Its Effect on CO2 Sorption Performance of Nano-Cao–catio3 Adsorbent

Hao Liu,Sufang Wu

DOI: https://doi.org/10.1080/09593330.2020.1800105

IF: 3.475

2020-01-01

Environmental Technology

Abstract:The aim of this work is to prepare the nano-CaO-CaTiO(3)adsorbents with both high CO(2)sorption capacity and high durability. A series of nano-CaO-CaTiO(3)adsorbents with different CaTiO(3)grain sizes werein situprepared by the reaction between TiO(2)and nano-CaO with variation of the preparation methods, doping contents and thermal pretreatment conditions. The results showed that the CaTiO(3)grain size would decrease by adopting the adsorption phase reaction method, reducing the doping content as well as thermal pretreatment temperature and time properly. Moreover, smaller CaTiO(3)grain size was favourable for increasing sorption capacity of the adsorbent, while larger CaTiO(3)grain size was more helpful for improving the durability. Under the consideration of the benefit of both the sorption capacity and the durability of adsorbents, the optimal CaTiO(3)grain size was got as 23.5 nm and its sorption capacity remained 8.52 mol/kg at the 50th cycle under the actual severe regeneration condition.
Study on the kinetics of Ca-based CO2 sorbent of carbonation and calcination for adsorption enhanced reforming process

Sufang Wu,Qi Shi,Qing Li

2008-01-01

Abstract:A nanoscale CaCO3 was used as precursor for CO2 adsorbent. The properties of calcination followed by carbonation were studied to pursue the reaction condition of as a criterion of reaction section and diffusion section. The simulation results showed that a relative deviation of CO2 adsorption ratio of the reaction section and diffusion section were lower than 3.5 and 0.86% respectively. The lower decomposition reaction condition under low CO2 partial pressure and easy to be regenerated of nanoscale Ca-based CO2 adsorbent were unparalleled. The nano Ca-based CO2 sorbent has an attractive potential to be used in the adsorption enhanced reforming process for producing hydrogen. This is an abstract of a paper presented at the 2008 AIChE Spring National Meeting (New Orleans, LA 4/6-10/2008).
A basic study on the nano CaO-based CO2 adsorbents in FFB for CO2 capture

Sufang Wu,Mingzhe Jiang,Rong Wu

2010-01-01

Abstract:In this paper, we study a nano CaO-based CO2 adsorbent obtained from a nano CaCO3 precursor by calcination. Nano CaO-based CO 2 adsorbents possess special features that underline their potential use in circulating fluidized beds coal gasification. A fixed fluid bed reactor was used to evaluate the target adsorbent, which was then analyzed using a thermo-gravimetric analyzer. The following properties were observed from the adsorbent produced: (1) lower carbonation and regeneration temperatures. This means energy savings in the CaCO3 regeneration looping system; (2) faster reaction rate with CO2. As such, the adsorbent meets the fast reaction needs of CFB systems; (3) higher sorption capacity of CO2, especially in fast reaction, and lower decay of sorption capacity; and (4) lower attrition loss during the looping process. Overall, the observed properties demonstrate the applicability of nano CaO-based CO2 adsorbents in CFB coal gasification and reactive sorption enhanced reforming.
Properties of a Nano CaO/Al2O3 CO2 Sorbent

Su Fang Wu,Qing H. Li,Jong N. Kim,Kwang Bok Yi

DOI: https://doi.org/10.1021/ie0704748

2007-01-01

Industrial & Engineering Chemistry Research

Abstract:This project studied the properties of nano CaO/Al2O3 as a high-temperature CO2 sorbent for its use in an adsorption enhanced reforming reaction. The sorbent containing nano CaCO3 precursors and aluminum oxide was prepared, and evaluation of the CO2 adsorption properties by a thermogravimetric analyzer, the results show that nano CaO/Al2O3 has a faster decomposition rate and has a higher CO2 adsorption ratio than micro CaO/Al2O3. The maximum adsorption ratio occurs at temperatures of 650 °C under a CO2 partial pressure of 0.33 atm. Durability studies show that the CO2 adsorption ratio remains at 68.3% after 50 cyclic runs under a carbonation temperature of 650 °C and calcination temperature of 800 °C, respectively. XRD, SEM, and BET were used for studying the change of micro characteristics of the CO2 sorbents before and after multiple carbonation−calcination runs. The results showed that the pore size of CaO/Al2O3 sorbents was enlarged and that a new substance (Ca12Al14O33) was formed even under a temperature of 800 °C for the function of keeping the compound stable and durable.
Preparation of Nano-CaCO3 from Phosphogypsum by Gas–Liquid–Solid Reaction for CO2 Sorption

Shang Qing Lu,Pei Qiang Lan,Su Fang Wu

DOI: https://doi.org/10.1021/acs.iecr.6b02551

2016-01-01

Industrial & Engineering Chemistry Research

Abstract:Nano-CaCO3 was prepared from phosphogyp-sum sum (PG) through reactive crystallization in the gas (CO2)-liquid (NH3-H2O) solid (PG) three-phase system. The effects of temperature, CO2 flow rate, and reaction time on the CaCO3 particle size distribution (PSD) were investigated. The results show that PG-derived nano-CaCO3 with an average particle diameter of 86-104 nm can be obtained under a 251-138 mL/min CO2 flow rate at a corresponding temperature of 30-40 degrees C. Research indicates that the CaCO3 particle size is subjected to the mutual influences of temperature, CO2 flow rate, and reaction time. A relatively low CO2 flow rate with increasing temperature and a strictly controlled reaction time are advantageous to the formation of nanosized CaCO3 grains. Additionally, PG-derived nano-CaO maintains a CO2 sorption capacity of 0.27 g of CO2/g of CaO after 10 calcination carbonation cycles, which is the same as for commercial nano-CaO.
Modified Kinetics Model of Nano CaO Reactions with CO2 in a CaO-Based Adsorbent

SHI Yu-yao,LAN Pei-qiang,WANG Yan,WU Su-fang

DOI: https://doi.org/10.3969/j.issn.1003-9015.2015.01.014

2015-01-01

Abstract:During the initial carbonation-calcination looping, the sorption capacity of nano CaO based adsorbent will decay and then keep stable. This study concerns the modified kinetics of nano CaO with CO2 in a CaO-based CO2 adsorbent after pretreatment of multiple looping cycles to reach stable reaction properties. The condition of pre-treatment included carbonation temperature of 600℃ and calcination temperature of 800℃ for 42 cyclic runs. The measurements of reaction rate were carried on a thermo-gravimetric analysis at 550~630℃ under a N2 atmosphere with 0.010~0.020 MPa CO2 mole pressures. A gas-solid ion reactive adsorption model was accepted for further parameters optimized. The modified gas-solid ion reactive adsorption kinetics model was then used for the simulation of experimental data. The simulation result of activation energy for carbonation of the pre-treated adsorbent is 77.7 kJ?mol?1 , which is 2.5 times than that of fresh nano CaO based adsorbent, and the average relative deviation of the CaO conversion is less than 6.4%. The reactive sorption rate in the fast surface reaction regime of nano CaO with CO2 is well represented by the modified gas-solid ion reactive adsorption model.
Behavior of CaTiO3/Nano-CaO As a CO2 Reactive Adsorbent

S. F. Wu,Y. Q. Zhu

DOI: https://doi.org/10.1021/ie900900r

2010-01-01

Industrial & Engineering Chemistry Research

Abstract:This study focuses on the preparation of a CaTiO3-coated nano-CaO-based CO2 adsorbent (CaTiO3/nano-CaO) for the improvement of sorption properties. The CaTiO3-coated nano-CaO adsorbent was prepared by forming Ti(OH)4 from the hydrolysis of titanium alkoxide in a nano-CaCO3 suspended solution. The resulting Ti(OH)4-coated nano-CaCO3 was then heated and calcined. Test results from transmission electron microscopy and scanning electron microscopy with energy dispersive X-ray spectroscopy show that an obvious film of TiO2 was formed on the surface of nano-CaCO3 after heating. X-ray diffraction analysis also showed that the nano-CaTiO3 layer was formed at 750 °C, a calcination temperature that causes the reaction of TiO2 with nano-CaO. The cyclic tests of reactive sorption capacity were conducted in a thermogravimetric analyzer under the following conditions: 0.02 MPa CO2 partial pressure, carbonation temperature of 600 °C, and calcination temperature of 750 °C. Test results showed that CaTiO3 coated onto the ...
Preparation of cage-like nano-CaCO3 hollow spheres for enhanced CO2 sorption

haoliang ping,sufang wu

DOI: https://doi.org/10.1039/c5ra12251a

IF: 4.036

2015-01-01

RSC Advances

Abstract:Cage-like nano-CaCO3 hollow spheres with different cavity diameters for CO2 sorption were prepared using the template-directed synthesis method. Carbon sphere templates with different diameters were synthesized via a hydrothermal reaction of starch under variable conditions. Field emission scanning electron microscopy (SEM) and transmission electron microscope (TEM) images indicated that the synthesized cage-like nano-CaCO3 hollow spheres had different cavity diameters of 0.52 mu m, 1.62 mu m and 2.93 mu m. The hollow sphere shells were composed of many uniform nanoparticles with diameters of approximately 80 nm, as supported by the X-ray diffraction (XRD) results. Furthermore, the CO2 sorption properties of the cage-like nano-CaCO3 hollow spheres were analyzed by thermo-gravimetric analysis (TGA). The sorption capacity of the optimum sample with a diameter of 1.62 mu m reached the maximal theoretical value of 0.786 g(CO2) g(CaO)(-1) at 600 degrees C and exceeded the sorption capacity of the reference nano-CaCO3 sorbents by 45%. The sorption properties of the sample within the rapid reaction stage at the different temperatures of 550 degrees C, 600 degrees C and 650 degrees C were also evaluated. The results demonstrated that the sample exhibited a 30% higher sorption rate than nano-CaCO3. Therefore, cage-like nanoCaCO(3) hollow spheres possess enhanced CO2 sorption capacity and higher sorption rates.
Formation of A Ca12al14o33 Nanolayer and Its Effect on the Attrition Behavior of Co2-Adsorbent Microspheres Composed of Cao Nanoparticles

Su F. Wu,Ming Z. Jiang

DOI: https://doi.org/10.1021/ie901561e

2010-01-01

Industrial & Engineering Chemistry Research

Abstract:The attrition behavior of microspheres composed of CaO nanoparticles that were used as high-temperature CO2-reactive adsorbents was investigated. The nano-CaO/Al2O3 microsphere adsorbents were prepared by a spray technique from a slurry containing a precursor of CaCO3 nanoparticles and an aluminum oxide gel. A mechanism of formation of the layer of nano-Ca12Al14O33 was proposed and optimized, with calcination temperatures ranging from 900 to 1000 degrees C and Ca/Al molar ratios between 2.3 and 3.5. The attrition behavior of the adsorbent was investigated in detail using the air jet method to measure fine loss, as well as with scanning electron microscopy and a particle size analyzer to examine the changes in surface morphology and particle size distribution. The attrition studies showed that complete formation of a Ca12Al14O33 nanoscale framework under calcination temperatures ranging from 900 to 1000 degrees C and Ca/Al molar ratios between 2.3 and 3.5 resulted in improved resistance to attrition and increased durability of the reactive sorption capacity of the adsorbent.
The Effect of CaO Content on Sorption Performance of Nano CaO Based CO2 Adsorbent

TANG Qi,WU Su-fang

DOI: https://doi.org/10.3969/j.issn.1003-9015.2012.01.006

2012-01-01

Abstract:The CO2 adsorbents with CaO contents of 6% to 100% were prepared by mixing the nano CaCO3 power with the alumina gel,and the effects of nano CaO content on the adsorption and microstructure properties of the CO2 adsorbent were studied.The results of microstructure property examinations show that,when the nano CaO content of CO2 adsorbent increases from 6% to 46%,the specific area decreases from 151.3 m2?g?1 to 8.1 m2?g?1,and the pore volume decreases from 0.41 cm3?g?1 to 0.07 cm3?g?1.However,when nano CaO content of CO2 adsorbent increases 27% to 46%,the pore size increases from 6.05 nm to 12.39 nm,and when CaO content is over 46%,the specific area and pore structure of the CaO adsorbents are similar to those of the pure CaO.The alumina in the adsorbent is amorphous when the CaO content is more than 27%,and the results of adsorption property experiments show that the adsorption capacity of nano CaO adsorbent increases from 1.02 mol CO2?g?1 to 7.05 mol CO2?g?1 when the CaO content increases from 12% to 83%.The adsorption rate becomes faster when CaO content of the CO2 adsorbent increases,and the results show that the relationship of CaO content to microstructure and adsorption properties of the nano CaO based adsorbents isn't linear.It was found that the stability of adsorption capacity and the adsorption rate of the CO2 adsorbent can be improved by adding a small amount of alumina.
Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Hua Pang,Anwei Sun,Haoran Xu,Gang Xiao

DOI: https://doi.org/10.1016/j.cej.2021.130675

IF: 15.1

2021-01-01

Chemical Engineering Journal

Abstract:MgO-based mixture is a promising candidate for CO2 capture due to its high theoritical capture capacity, noncorrosiveness, low cost and wide availability. In this work, the effects of preparation methods and sorption conditions on the characteristics of MgO-Na2CO3 are studied. A stable MgO conversion of 0.32 for CO2 sorption is obtained during the 30-cycle tests at 400 degrees C, 2 MPa, where the material exhibits a strong skeleton structure with increased specific surface area when prepared by the ball-milling method. A severe sorption condition of 500 degrees C, 3 MPa is also tested, where the material shows a stable MgO conversion of 0.3 after 20 cycles. With the increase of Na2CO3 content in the mixture, a higher MgO conversion can be achieved, but the cyclic stability will be impaired. In addition to the experiments, density function theory calculations are conducted to explore the sorption mechanism of MgO-Na2CO3, where CO2 adsorptions on the pure, the Na-doped, and the Na2CO3-MgO co-adsorption surfaces are compared. The defect is found to help induce electrons from the Na and Mg atoms to the CO2 molecule, thus benefiting the CO2 adsorption process. The presence of Na2CO3 also benefits the adsorption process of MgO due to its electrostatic interaction with CO2 molecules. This work can serve as the guideline for the design of MgO-based CO2 absorbent especially for extreme operating conditions.
Properties of a Nano CaO/Al2O3CO2Sorbent

Su F. Wu,Qing H. Li,jong nam kim,kwang bok yi

DOI: https://doi.org/10.1021/ie0704748

2008-01-01

Industrial & Engineering Chemistry Research

Abstract:This project studied the properties of nano CaO/Al2O3 as a high-temperature CO2 sorbent for its use in an adsorption enhanced reforming reaction. The sorbent containing nand CaCO3 precursors and aluminum oxide was prepared, and evaluation of the CO2 adsorption properties by a thermogravimetric analyzer, the results show that nano CaO/Al2O3 has a faster decomposition rate and has a higher CO2 adsorption ratio than micro CaO/Al2O3. The maximum adsorption ratio occurs at temperatures of 650 degrees C under a CO2 partial pressure of 0.33 atm. Durability studies show that the CO2 adsorption ratio remains at 68.3% after 50 cyclic runs under a carbonation temperature of 650 C and calcination temperature of 800 degrees C, respectively. XRD, SEM, and BET were used for studying the change of micro characteristics of the CO2 sorbents before and after multiple carbonation-calcination runs. The results showed that the pore size of CaO/Al2O3 sorbents was enlarged and that a new substance (Ca12Al14O33) was formed even under a temperature of 800 degrees C for the function of keeping the compound stable and durable.
Performance of Nano-Caco3 Coated with SiO2 on CO2 Adsorption at High Temperature

WU Rong,WU Sufang

DOI: https://doi.org/10.3321/j.issn:0438-1157.2006.07.041

2006-01-01

Abstract:Nano-CaCO_3 particles were surface-coated with SiO_2 by the sol-gel method and used as the high temperature CO_2 adsorption material.CaCO_3 samples prepared at 60—90℃ were characterized with TEM, EDS and XRD methods and the initial and final decomposition temperature were determined with TGA.The CO_2 adsorption ratio and carbonation-calcination characteristics were evaluated in a 12 mm fixed bed reactor.The analytical results showed that there was an amorphous SiO_2 film formed on the surface of nano-CaCO_3,and the atomic ratio of Si to Ca is 1∶39.The initial and final decomposition temperatures were 595—620℃ and 800—820℃ respectively.The maximum CO_2 adsorption ratio of SiO_2 coated with nano-CaCO_3 was 92.1% at 600℃with a 10% increase as compared with the uncoated nano-CaCO_3 particles.After 20 cyclic carbonation and calcination runs, CO_2 adsorption ratio of the SiO_2 coated samples was 63%.The XRD analysis illustrated that the crystal type of nano-CaCO_3 had no change after 20 cyclic runs.
Preparation of High Sorption Durability Nano-CaO–ZnO CO2 Adsorbent

Hao Liu,Sufang Wo

DOI: https://doi.org/10.1021/acs.energyfuels.9b01770

IF: 4.6541

2019-01-01

Energy & Fuels

Abstract:ZnO was doped into nano-CaO adsorbents to increase the sorption durability in the calcium looping (CaL) process. The preparation of a nano-CaO–ZnO adsorbent was studied in detail by varying the ZnO additive amounts and thermal pretreatment conditions. Also, the performance of the nano-CaO–ZnO adsorbent was evaluated under different CaL operation conditions. The results showed that the carbonation conversion of CaO in the adsorbent was stably kept as 57.4% after 15 cycles when the optimum values of the molar ratio of CaO to ZnO was 8, thermal pretreatment temperature and time were 850 °C and 1 h, respectively, and the carbonation and regeneration temperatures were 700 and 750 °C, respectively. The anti-sintering performance of ZnO was close to that of ZrO2 and TiO2 and better than that of MgO and Al2O3. The reason for the high durability of the nano-CaO–ZnO adsorbent was that low thermal expansibility dopant ZnO, could promote the recurrence of nano-CaO grains, leading to self-reactivation in the CaL process.
Mn-promoted CaO-based adsorbents with enhanced CO2 uptake performance

Yonghui Xu,Baohua Xiao,Yanyan Feng,Wen Yang,Yiju Lv

DOI: https://doi.org/10.1016/j.jngse.2021.104029

IF: 5.285

2021-10-01

Journal of Natural Gas Science and Engineering

Abstract:The adsorption of CO2 over CaO-based adsorbents has been an effective way to capture CO2 at high temperature, but the adsorption capacity was hampered and the cycle durability was poor. To address the said problems, this paper reported the effect of Mn doping on the structure, morphology and CO2 adsorption performances of CaO-based adsorbents synthesized by a sol-gel method. The characterization results showed that the addition of Mn was helpful to form abundant micropores and mesopores in the doped CaO-based adsorbent, and Mn can effectively prevent the sintering and agglomeration of CaO particles. Moreover, electron transfer occurred on the modified CaO-based absorbents. These findings suggested that Mn species induced both structural and electronic promotion effect, resulting in smaller particle, higher dispersion and specific surface area of CaO-based adsorbents and formation of some electron-rich oxygen and Ca species, ultimately boosting CO2 adsorption performance. Especially, with the molar ratio of Ca/Mn being 20, the adsorbent Ca/Mn-20 presented the best CO2 uptake and excellent cycle stability (up to 10 cycles). In addition, it can be concluded that the adsorption process of CO2 was more obedient to the pseudo-second-order kinetic model, indicating the adsorption process was dominated by chemical adsorption.

energy & fuels,engineering, chemical
Efficient MgO-doped CaO sorbent pellets for high temperature CO2 capture

Zhihong Xu,Tao Jiang,Hao Zhang,Yujun Zhao,Xinbin Ma,Shengping Wang

DOI: https://doi.org/10.1007/s11705-020-1981-2

IF: 4.803

2021-01-04

Frontiers of Chemical Science and Engineering

Abstract:Novel MgO-doped CaO sorbent pellets were prepared by gel-casting and wet impregnation. The effect of Na+ and MgO on the structure and CO2 adsorption performance of CaO sorbent pellets was elucidated. MgO-doped CaO sorbent pellets with the diameter range of 0.5–1.5 mm exhibited an excellent capacity for CO2 adsorption and adsorption rate due to the homogeneous dispersion of MgO in the sorbent pellets and its effects on the physical structure of sorbents. The results show that MgO can effectively inhibit the sintering of CaO and retain the adsorption capacity of sorbents during multiple adsorption-desorption cycles. The presence of mesopores and macropores resulted in appreciable change of volume from CaO (16.7 cm3·mol−1) to CaCO3 (36.9 cm3·mol−1) over repeated operation cycles. Ca2Mg1 sorbent pellets exhibited favorable CO2 capture capacity (9.49 mmol·g−1), average adsorption rate (0.32 mmol·g−1·min−1)and conversion rate of CaO (74.83%) after 30 cycles. 

engineering, chemical
In situ preparation of CaTiO 3 and its effect on CO 2 sorption performance of nano-CaO–CaTiO 3 adsorbent

Hao Liu,Sufang Wu

DOI: https://doi.org/10.1080/09593330.2020.1800105

IF: 3.475

2020-08-06

Environmental Technology

Abstract:The aim of this work is to prepare the nano-CaO–CaTiO3 adsorbents with both high CO2 sorption capacity and high durability. A series of nano-CaO–CaTiO3 adsorbents with different CaTiO3 grain sizes were in situ prepared by the reaction between TiO2 and nano-CaO with variation of the preparation methods, doping contents and thermal pretreatment conditions. The results showed that the CaTiO3 grain size would decrease by adopting the adsorption phase reaction method, reducing the doping content as well as thermal pretreatment temperature and time properly. Moreover, smaller CaTiO3 grain size was favourable for increasing sorption capacity of the adsorbent, while larger CaTiO3 grain size was more helpful for improving the durability. Under the consideration of the benefit of both the sorption capacity and the durability of adsorbents, the optimal CaTiO3 grain size was got as 23.5 nm and its sorption capacity remained 8.52 mol/kg at the 50th cycle under the actual severe regeneration condition.

environmental sciences

Preparation of MgO-coated Nano CaO Using Adsorption Phase Reaction Technique for CO2sorption

Synthesis of a Porous Nano‐CaO/MgO‐Based CO2 Adsorbent

A new nano CaO-based CO2 adsorbent prepared using an adsorption phase technique

Adsorption Properties of Coating Modified Nano CaO-Based CO2 Adsorbents

In Situ Preparation of CaTiO3 and Its Effect on CO2 Sorption Performance of Nano-Cao–catio3 Adsorbent

Study on the kinetics of Ca-based CO2 sorbent of carbonation and calcination for adsorption enhanced reforming process

A basic study on the nano CaO-based CO2 adsorbents in FFB for CO2 capture

Properties of a Nano CaO/Al2O3 CO2 Sorbent

Preparation of Nano-CaCO3 from Phosphogypsum by Gas–Liquid–Solid Reaction for CO2 Sorption

Modified Kinetics Model of Nano CaO Reactions with CO2 in a CaO-Based Adsorbent

Behavior of CaTiO3/Nano-CaO As a CO2 Reactive Adsorbent

Preparation of cage-like nano-CaCO3 hollow spheres for enhanced CO2 sorption

Formation of A Ca12al14o33 Nanolayer and Its Effect on the Attrition Behavior of Co2-Adsorbent Microspheres Composed of Cao Nanoparticles

The Effect of CaO Content on Sorption Performance of Nano CaO Based CO2 Adsorbent

Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Properties of a Nano CaO/Al<sub>2</sub>O<sub>3</sub>CO<sub>2</sub>Sorbent

Performance of Nano-Caco3 Coated with SiO2 on CO2 Adsorption at High Temperature

Preparation of High Sorption Durability Nano-CaO–ZnO CO2 Adsorbent

Mn-promoted CaO-based adsorbents with enhanced CO2 uptake performance

Efficient MgO-doped CaO sorbent pellets for high temperature CO2 capture

In situ preparation of CaTiO 3 and its effect on CO 2 sorption performance of nano-CaO–CaTiO 3 adsorbent