Preparation of La,Y-Mo Powder by the Sol-Gel Method

W Liu,ML Zhou,JS Wang,YX Chen,DW Zheng

DOI: https://doi.org/10.3321/j.issn:1002-185x.2005.02.029

2004-01-01

The Chinese Journal of Nonferrous Metals

Abstract:The La, Y-Mo composite oxide powder was successfully prepared by the Sol-Gel method. The technique terms are as follows: the pH value of the precursor solution is 1; the decomposition temperature is 550 degreesC. The reduction temperature of the first step is 500degreesC and of the second 900degreesC. The composition, microgram and granularity of the powder are studied by the XRD,SEM, etc. The results show that the molybdenum appear after the reduction at 500degreesC and the rare earth elements consist in the structure of RE-O-Mo. After the second reduction, the rare earth elements consist with the form of the rare earth oxide. The results from the infrared spectrum (FT-IR) show that the bond of the Mo = O is weakened due to the bond of the RE-O-Mo, leading to the increase of the reduction properties of the RE-Mo composite oxide powders. The results also show that the granularity of the RE-Mo powder is about 70 nm.