Abstract:Due to the low content of silicon and aluminum in red mud and the low reaction activity of red mud, when it was used to prepare composite cementitious materials, it was necessary to assist other aluminosilicates and improve their activity by certain methods. In this study, it was proposed to add slag to increase the percentage of silicon and aluminum in the system, and to improve the reactivity of the system through the activation effect of sulfate in phosphogypsum. The effects of slag and phosphogypsum contents on the mechanical properties and microstructures of composite cementitious materials were studied. X-ray diffraction analysis (XRD), thermogravimetric analysis (TG-DTG), and scanning electron microscopy (SEM) were used to analyze the effects of slag and phosphogypsum contents on the hydration products, microstructure, and strength formation mechanism of composite cementitious materials. The results show that with the increase of slag, the strength of the composite cementitious material increases gradually. When the slag content is 50%, the 28-day compressive strength reaches a maximum of about 14 MPa. Compared with the composite material without phosphogypsum, the composite cementitious material with 10–20% phosphogypsum showed higher strength properties, in which the 28-day compressive strength exceeds 24 MPa. The main reason for this is that the sulfate in phosphogypsum can cause the composite cementitious material to generate a large amount of ettringite and accelerate the dissolution of red mud and slag, increasing the release of aluminates, silicates, and Ca2+ to form more C-(A)-S-H and ettringite. In addition, a large amount of C-(A)-S-H makes ettringite and unreacted particles combine into a uniform and compact structure, thus improving the strength. When the content of phosphogypsum exceeds 40%, the 28-day compressive strength of the composite cementitious material drops below 12 MPa due to the presence of fewer hydration products and the expansion of ettringite.

Hydration Characteristics of Intermediate-Calcium Based Cementitious Materials from Red Mud and Coal Gangue

Hydration Characteristics of Red-Mud Based Paste-Like Backfill Material

Hydration Mechanism and Leaching Behavior of Bauxite-Calcination-method Red Mud-Coal Gangue Based Cementitious Materials.

Hydration kinetics of cementitious materials composed of red mud and coal gangue

Hydrated Properties and Mineralogical Composition of Sulphoaluminate Cement Clinker Made from Red Mud

Pozzolanic Behaviour of Compound-Activated Red Mud-Coal Gangue Mixture

Study on Hydration and Hardening Performance of Coal Gangue-Steel Slag-Cement Composite Cementitious Material

Carbonation and Related Behaviors of Hardened Cement Pastes under Different Hydration Degrees

Effect of Red Mud on Mechanical Properties of Loess–Containing Aluminosilicate Based Cementitious Materials

Microstructure and Key Properties of Phosphogypsum-Red Mud-Slag Composite Cementitious Materials

Formation mechanism and thermal decomposition properties of hydration products of superfine tailings cemented paste backfill

Co-utilization of reactivated cement pastes with coal gangue

Synergistic Activation Mechanism and Long-Term Properties of a Solid Waste Cementitious Materials Based on Red Mud and Calcium Carbide Slag

Evaluation of blends bauxite-calcination-method red mud with other industrial wastes as a cementitious material: properties and hydration characteristics.

Structural investigation relating to the cementitious activity of bauxite residue — Red mud

Strengthening Mechanism of Red Mud with Calcium Oxide

Effect of pore structure characteristics on the properties of red mud-based alkali-activated cementitious materials

Study on Rheological Mechanism of Cement-Coal Gangue Cementitious Material (CGCM) Slurry

Hydration Mechanism and Phase Assemblage of Blended Cement with Iron-Rich Sewage Sludge Ash

Influence of Hardened Paste Microstructure on Rheological Property of Cementing Slurries with High Density