Abstract:In this paper, we discussed recent studies done in our laboratories with a floating catalyst chemical vapor deposition (CVD) method. We can grow single- or double-walled carbon nanotubes (SWNTs/DWNTs) with different kinds of catalysts. Single-walled carbon nanotubes without amorphous carbon coating were prepared by thermally decomposing acetylene (C2H2) at the temperature range of 750–1200°C with ferrocene as catalyst. While with sulfur promoted ferrocene catalyst, double-walled carbon nanotubes were mass-produced by pyrolizing C2H2 at the temperature range of 900–1100°C. Furthermore, tunable growth of DWNTs with different diameter was achieved in our experiment. It is found that DWNTs produced at lower carbon partial pressure have much smaller inner tubes, even DWNTs with the smallest inner diameter of 0.4nm was found in here. As convenient and effective tool, radial breathing mode (RBM) of Raman scattering technique can be used to distinguish SWNTs from DWNTs. In further studies of Raman scattering with DWNTs, the possible match of the inner tubes and the outer tubes according to the RBM bands was assigned, and different chirality types were discussed according to the diameter and chirality dependence of resonant Raman vibration. We also investigated the temperature-dependent frequency shift of resonant Raman spectra of DWNTs in the range of 78–650K. We found that different RBM peaks, which are relative to different tube diameters, have different temperature coefficient of frequency shift, and the larger diameter carbon nanotubes have more RBM frequency downshift with increasing temperature. It is ascribed to the RBM frequency variation to the temperature dependence of the stretching force constant of C–C bond. Besides, Polarized Raman spectra were preformed on well-aligned SWNTs structure fabricated through post-growth method and found that the angular dependence of Raman intensity is consistent well with the predictions of the resonance Raman theory.

Synthesize Single-Wall Carbon Namotubes by Low-Pressure Chemical Vapor Deposition Method

Large scale CVD synthesis of single-walled carbon nanotubes

CVD synthesis of single-walled carbon nanotubes by Co/MgO solid catalysts

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

High-Quality Single-Walled Carbon Nanotubes Synthesized by Floating Catalyst Chemical Vapor Depostion

Synthesis Of High Quality Single-Walled Carbon Nanotubes By Cvd And Effect Of Catalyst'S Acidity-Basicity On Nanotubes Growth

Large- Scale Production of Single- Walled Carbon Nanotubes Using Fe/Mo/MgO Cryogel Catalyst

Subnanometer Single-Walled Carbon Nanotube Growth from Fe-Containing Layered Double Hydroxides

Catalyst Design Using Nanoporous Iron for the Chemical Vapor Deposition Synthesis of Single-Walled Carbon Nanotubes

Synthesis of vertically aligned single-walled carbon nanotubes with sub-nanometer-diameter using cobalt-copper binary catalyst

Large-Scale Synthesis and Magnetic Property of Carbon Nanotubes

A Scalable CVD Synthesis of High-Purity Single-Walled Carbon Nanotubes with Porous MgO As Support Material

Controlled Growth of Single-Walled Carbon Nanotubes at Atmospheric Pressure by Catalytic Decomposition of Ethanol and an Efficient Purification Method

High-Density Growth of Single-Wall Carbon Nanotubes on Silicon by Fabrication of Nanosized Catalyst Thin Films

Controllable preparation and properties of single-/double-walled carbon nanotubes

Narrow-chirality distributed single-walled carbon nanotube synthesized from oxide promoted Fe–SiC catalyst

Preparation of monodispersed multi-walled carbon nanotubes in chemical vapor deposition

Production of High Quality Single-Walled Carbon Nanotubes in a Nano-Agglomerated Fluidized Bed Reactor

Synthesis of subnanometer-diameter vertically aligned single-walled carbon nanotubes with copper-anchored cobalt catalysts

Cvd Synthesis and Diameter Distribution of Single-Walled Carbon Nanotubes

CVD Growth of Carbon Nanotube Forest with Selective Wall-Number from Fe–Cu Catalyst