Abstract:Nanocrystalline Ce-substituted yttrium iron garnet (YIG) powders of different compositions, Y3-x Ce x Fe5O12 (0 ≤ x ≤ 2.0), were synthesized by a combination of sol-gel auto-combustion and solid-state synthesis techniques. The as-obtained powder samples were sintered at 1150 °C for 10 h. The garnet structure formation is confirmed by the X-ray diffraction pattern, which shows that the calculated lattice parameter increased for x = 1.0 and shows a decreasing trend for x ≥ 1.0 with the addition of cerium ions. The lattice parameter increased from 12.38 Å to 12.41 Å for x ≤ 1.0 whereas it decreased from 12.412 Å to 12.405 Å with the cerium composition for x > 1.0. The average particle size determined by high resolution transmission electron microscopy is in the range of 50 to 90 nm and found to increase with the substitution of cerium ions in YIG. The room temperature magnetic parameters such as saturation magnetization, coercivity and remanence magnetization are greatly affected by the substitution of cerium ions. The values of saturation magnetization decrease from 25.5 to 15 emu g-1 whereas coercivity increases from 1 to 28 Oe with the substitution of cerium ions. The pure YIG sample shows polycrystalline nature that changed towards a single-crystal structure leading to a preferred-(100) orientation with the Ce substitution. The change from a ring to a spotty pattern observed in SAED confirmed the crystalline phase transformation and is well supported by HRTEM and magnetic measurements. The behavior of magnetic and electrical properties is well supported by the poly- and single-crystalline nature of YIG and Ce-YIG, respectively. The crystal structure transformation in YIG brought about by Ce substitution could unveil enormous opportunities in the preparation of single-crystal materials from their polycrystalline counterparts.

Preparation and Characterization of Nanophase Ce:YIG Magnetic Powder by Coprecipitation

Preparation of Ce-substituted yttrium iron garnets (Ce:YIG)

Polycrystalline to preferred-(100) single crystal texture phase transformation of yttrium iron garnet nanoparticles

Structure and Magnetic Properties of Ce-Substituted Yttrium Iron Garnet Prepared by Conventional Sintering Techniques

Solid Phase Synthesis and Sintering Properties of Yttrium Iron Garnet

Preparation of YIG Single Crystal Nanofibers Via an Electrospinning Technique

Synthesis and analysis of the magnetic properties of YIG by means of sol–gel and spark plasma sintering

GELATION AND ANNEALING PROCESS OF PREPARING NANOCRYSTALLINE Y3Fe5O12 (YIG) BY SOL-GEL METHOD

Low-temperature Solution Synthesis and Characterization of Ce-doped YAG Nanoparticles

A New Approach of Preparing Nanocrystalline Bi-YIG Films

Preparation and Luminescence Property of YAG : Ce Phosphor Powders by Co-precipitation

Research of preparing Bi substituted yttrium iron garnet and epoxy magneto-optical hybridized films

PREPARATION AND PHOTOLUMINESCENCE PROPERTIES OF YAG:Ce3+ SPHERICAL PHOSPHOR NANO-POWDERS BY THE MICROEMULSION METHOD

Study on Synthesis of Y_(3-x)Ce_xAl_5O_(12) Nanopowders by Sol-gel Method

Preparation and annealing process of Y3Fe5O12 by sol-gel method

Sintering and electrical properties of coprecipitation prepared Ce0.8Y0.2O1.9 ceramics

Synthesis of YAG:Ce phosphor by impinging streams co-precipitation method

MAKING MAGNETO-OPTIC CE-SUBSTITUTED YIG THIN FILMS ON AMORPHOUS SILICA SUBSTRATE

Microstructures and Magnetic Properties of Single-Step Deposited Ce:YIG/YIG Bilayer Films with Different Layer Thickness Ratios

Study of Cerium Ion in (Y0.95la0.05)(2)o-3:Ce

Synthesis of Yig Nanopowders by Sol-Gel Method