Abstract:Using metal nitrates as starting materials and citric acid as complexing agent, Y3Al5O12 : Ce3+ (YAG: Ce3+) phosphor was prepared by inorganic-organic hybrid gel method. The formation process of Y3Al5O12 (YAG, Yttrium Aluminum monoclinic) phase was investigated by means of XRD. The results show that the YAG phase can be formed by two routs, one is the direct phase transformation from amorphous ytterium oxide and aluminium oxide to YAG phase, another is a two steps process from amorphous ytterium oxide and aluminium oxide to YAlO3(YAP) and gamma-Al2O3 intermediate phases, and then turn to YAG. The YAG: Cc 3, phosphor with pure crystalline phase was obtained at 900degreesC, which is 600degreesC lower than that of conventional solid reaction method. This phosphor absorbs excitation energy in the range 403 similar to 510nm with the maximum excitation wavelength at near 459nm and shows a yellow emission in the range 480 similar to 650nm with maximum intensity at 550nm. At the same time, this phosphor was coated with Al2O3 and La2O3 by using sol-gel method and hydroxide precipitation method respectively. The photoluminescence properties of the coated phosphors were also investigated comparatively by treating the phosphor in hot oxidation atmosphere, acid and base solution. It was found that a slight decrease of luminescence intensity and an improvement in phosphor maintenance was observed due to the surface modification of phosphors caused by coating.

Preparation and Luminescence Property of YAG : Ce Phosphor Powders by Co-precipitation

Influences of preparation conditions on luminescent performance of Ce-doped Y_3Al_5O_(12) phosphor powders

PREPARATION AND PHOTOLUMINESCENCE PROPERTIES OF YAG:Ce3+ SPHERICAL PHOSPHOR NANO-POWDERS BY THE MICROEMULSION METHOD

Co-precipitation synthesis and luminescence behavior of Ce-doped yttrium aluminum garnet (YAG:Ce) phosphor: The effect of precipitant

Synthesis of YAG:Ce phosphor by impinging streams co-precipitation method

Synthesis of (Y, Gd)3Al5O12:Ce Nanophosphor by Co-Precipitation Method and Its Luminescence Behavior

Microstructure and Luminescence Characteristics of YxAl5O12∶Ce3+Phosphor

Sol-Gel Synthesis of YAG∶Ce Phosphor and Luminescence Properties

Citrate sol-gel combustion preparation and photoluminescence properties of YAG:Ce phosphors

The Effect of Ce3+ Concentration and Heat Treatment on the Luminescence Efficiency of YAG Phosphor

Preparation and luminescent properties of Y 2.9Ce 0.1Al 5O 12 nano-phosphors by hydrothermal treatment and post-annealing process

Comparative investigation on synthesis and photoluminescence of YAG:Ce phosphor

Tailored Photoluminescence of YAG:Ce Phosphor Through Various Methods

Effect of Sintering Time on Luminescent Properties of YAG: Ce3+ Phosphors

Coating And Stability Of Yag : Ce3+ Phosphor Synthesized Using Inorganic-Organic Hybrid Gel Method

Yag : Ce3+ Nanopowders: Synthesis, Characteristics And Luminescent Properties

Synthesis of High-Performance YAG:Ce Phosphor Powder with Low Sintering Temperature and YAG:Ce-Doped Bi-B Glass by a One-Step Method

Enhanced Photoluminescence Property of Sulfate Ions Modified YAG:Ce3+ Phosphor by Co-Precipitation Method

Photoluminescence investigations of (Y1-xLnx)3Al5O12:Ce (Ln3+=Gd3+, La3+) nanophosphors

Low-temperature Solution Synthesis and Characterization of Ce-doped YAG Nanoparticles

Preparation of CaYAl3O7:Ce3+, Tb3+ Blue-Green Phosphors by Sol-Gel Process