Synthesis of Ce3+ Doped Y3Al5O12 and Its VUV Spectral Characteristics
SHEN Lei-jun,ZHAO Zeng-qi,WAN Zuo-bo,ZHOU Yong-bo,LI Bo,ZHANG Guo-bin
2008-01-01
Abstract:The Y3-xAl5O12∶Ce3+x(x=0.01,0.03,0.05,0.07,0.09)samples were synthesized by the conventional solid state reaction method as well as co-precipitation method. XRD analysis shows that the synthesized samples are all in single lattice phase with cubic structure,which is consistent with the JCPDS standard card (88-2047). From the SEM analyses, the use of co-precipitation method decreases the synthesis temperature of the samples, and results in fine grains and particles in these materials. In the VUV excitation spectrum of YAG∶Ce, three separative peaks are found at 126 nm, 177 nm and 230 nm, respectively. There is a wide asymmetry emission band peaked at about 530～540 nm, and resulted from two transitions of 5d→2F5/2 and 5d→2F7/2 of Ce3+ in the PL emission spectra. The intensity of emission spectra of Y3-xAl5O12∶Ce3+x(x=0.01,0.03,0.05,0.07,0.09)increases as x increases from 0. 01 to 0.05, and then decreases when x increases from 0. 05 to 0.09 further. The phenomenon accords with characteristic concentration quenching.