Abstract:As a promising replacement for nitride red phosphors, Ce: Y3(Mg1.8Al1.4Si1.8)O12(Ce: YMASG) ceramic phosphors have attracted significant attention recently for their advantages in inorganic encapsulation and massive red‐shifting of Ce3+ emission. In this work, Ce: YMASG with different doping concentrations of Ce3+ and Al2O3, was fabricated by vacuum sintering to investigate its effects on the elimination of the impurity phase and the enhancement of the luminescent properties of white light‐emitting diodes (w‐LEDs). It was discovered that the emission wavelength redshifts from 592 nm to 606 nm as the Ce3+ concentration increases, while at 450 K, the emission intensity deteriorates from 0.47 to 0.36 of its initial value. The Rietveld analysis revealed the presence of an impurity phase of Y4MgSi3O13 with a concentration of 17.021 wt% in Ce: YMASG. With the introduction of Al2O3, the impurity phase was eliminated from the matrix completely, the emission peak shifted to a shorter wavelength, and the thermal stability was greatly improved. When the correlated color temperature was controlled at around 3000 K in the packaged w‐LEDs, the commission international de l'éclairage (CIE) chromaticity coordinates shifted toward the bottom left corner of the diagram with increasing concentration of Ce3+. Conversely, the luminous efficiency (LE) increased from 36 lm/W to 58.6 lm/W as the concentration of Al2O3 increased from 0 to 10 wt%, which demonstrated the application prospect of the fabricated phosphor in warm w‐LEDs.

Citrate sol-gel combustion preparation and photoluminescence properties of YAG:Ce phosphors

Study on Preparation of Orange-Emitting Phosphor Y3Mg2AlSi2O12: Ce3+ for Wled

Coating And Stability Of Yag : Ce3+ Phosphor Synthesized Using Inorganic-Organic Hybrid Gel Method

Synthesis of YAG:Ce phosphor by impinging streams co-precipitation method

PREPARATION AND PHOTOLUMINESCENCE PROPERTIES OF YAG:Ce3+ SPHERICAL PHOSPHOR NANO-POWDERS BY THE MICROEMULSION METHOD

Tunable luminescence Y3Al5O12:0.06Ce 3+, xMn2+ phosphors with different charge compensators for warm white light emitting diodes

Effect of Sintering Time on Luminescent Properties of YAG: Ce3+ Phosphors

Photoluminescence and Thermoluminescence of Ce3+ Incorporated Y3Al5O12 Synthesized by Rapid Combustion

Tunable luminescence Y_3Al_5O_12:006Ce^3+, xMn^2+ phosphors with different charge compensators for warm white light emitting diodes

Low-temperature Solution Synthesis and Characterization of Ce-doped YAG Nanoparticles

Synthesis of High-Performance YAG:Ce Phosphor Powder with Low Sintering Temperature and YAG:Ce-Doped Bi-B Glass by a One-Step Method

Crystal Structure and Photo-Luminescence of Gd3Ga2(Al3-ySiy)(O12-yNy):Ce3+ Phosphors for AC-warm LEDS

Preparation of CaYAl3O7:Ce3+, Tb3+ Blue-Green Phosphors by Sol-Gel Process

Solution Combustion Synthesis and Enhanced Luminescence of Eu3+-activated Y2Ce2O7 Phosphor Nanopowders

Molten Salt Synthesis of YAG:Ce3+ Phosphors from Oxide Raw Materials

Structural, Luminescent Properties and Chemical State Analysis of YAG:Ce Nanoparticle-Based Films

Optimization of Ce 3+ concentration and Y 4 MgSi 3 O 13 phase in Mg 2+ ‐Si 4+ Co‐doped Ce: YAG ceramic phosphors

Yag : Ce3+ Nanopowders: Synthesis, Characteristics And Luminescent Properties

Synthesis-dependent luminescence properties of Y3Al5O12:Re3+ (Re=Ce, Sm, Tb) phosphors

Photoluminescence Enhancement of YAG:Ce Nanophosphors with SiO2 Additions

Crystallization and Fluorescence Properties of Ce:Yag Glass-Ceramics with Low Sio2 Content