Abstract:We presented a study on the structure and magnetic properties of yttrium iron garnet (YIG), Y 3 Fe 5 O 12 , which was synthesized by means of sol–gel method and spark plasma sintering (SPS). The YIG nanoparticles were prepared by sol–gel method followed by 800 °C annealing for 3 h. SPS procedures with different temperatures (700 °C∼900 °C) and holding times (30 min ∼ 90 min) were performed to study the influence of SPS conditions on the structure and magnetic properties of YIG. The X-ray diffraction pattern and Raman spectrum confirmed the presence of YIG at all studied conditions. All samples were pure garnet phase except for the samples with too high temperatures (900 °C) and too long holding time (90 min). The impurities were inferred to be due to the hypoxic environment caused by the vacuum sintering condition of SPS. The magnetic properties of YIG samples were significantly affected by SPS conditions. The YIG sample became multi-domain at the temperature as low as 750 °C and grew to 89.1 nm at 850 °C for 30 min holding time benefiting from to the special sintering effect of SPS. Large particles with loose texture were formed by the formation of sintering neck between the adjacent particles when the SPS temperature was higher than 800 °C. It are confirmed that the sample with extended holding time at a moderate temperature (800°C/60 min) show the best soft-magnetic properties, whose M s , M r and H c are 27.5 emu/g, 2.4 emu/g and 19.2 Oe respectively. The results show that this method has good potential in preparing YIG with good magnetic properties.

Synthesis of Yig Nanopowders by Sol-Gel Method

GELATION AND ANNEALING PROCESS OF PREPARING NANOCRYSTALLINE Y3Fe5O12 (YIG) BY SOL-GEL METHOD

Preparation and annealing process of Y3Fe5O12 by sol-gel method

Solid Phase Synthesis and Sintering Properties of Yttrium Iron Garnet

Synthesis and analysis of the magnetic properties of YIG by means of sol–gel and spark plasma sintering

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

A New Approach of Preparing Nanocrystalline Bi-YIG Films

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Preparation of YAG Nanoparticles by Sol-Gel and Their Application in Electrical Contact Material

Preparation of YIG Single Crystal Nanofibers Via an Electrospinning Technique

Synthesis and characterization of yttrium iron garnet (YIG) nanoparticles - Microwave material

Synthesis of nanoscaled yttrium aluminum garnet powder by the co-precipitation method

Nanoscaled YAG Powders Via Coprecipitation Using Ammonium Hydrogen Carbonate As the Precipitant

Study on Synthesis of Y_(3-x)Ce_xAl_5O_(12) Nanopowders by Sol-gel Method

The Effect of pH value on the nano-particle size of bi substituted yttrium iron garnet

Preparation of Rare Earth/Alkaline Earth Composite Silicates Nanopowder by Water-Based Sol-Gel Method

Low‐Temperature Synthesis of Nanocrystalline Yttrium Aluminum Garnet Powder Using Triethanolamine

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

Influence of Surfactants on Co-Precipitation Synthesis of Bi–YIG Particles

Study on the Structure, Magnetic Properties and Mechanism of Zn-Doped Yttrium Iron Garnet Nanomaterial Prepared by the Sol-gel Method

Yag : Ce3+ Nanopowders: Synthesis, Characteristics And Luminescent Properties